关于大矿批、高煤比在高炉操作中应用.pdfVIP

关于大矿批、高煤比在高炉操作中的应用 徐艳波 孟宪慧 王云丽 王立杰 （唐山不锈钢公司，唐山 063000 ） 摘 要 随着炼铁原燃料价格的不断上涨，进一步改善煤气利用，降低消耗提高指标，是摆在我们炼铁操作者面前 的首要课题。不锈钢公司450 高炉尝试了高煤比、大矿批。首先，450 高炉采用多环布料，矿批由 18t 扩到 25t，随 之扩到 27t ，高炉顺行没有受到影响，指标反而得到明显好转。 关键词 大矿批 高煤比 富氧1 About Large Ore Batch and High Coal Rate Application of the Blast Furnace Operation Xu Yanbo Meng Xianhui Wang Yunli Wang Lijie (Tangshan Stainless Steel Co.,Ltd., Tangshan,063000) Abstract With the iron raw material and fuel prices continue to rise, further improve the gas utilization, reduce consumption and improve the indicators, is placed in front of the operator we iron the most important issue. 450 stainless steel blast furnace in the company tried a high coal ratio, large ore batch. First, multi-loop fabric 450 blast, the mine expansion approved by the 18 tons to 25 tons, along with expansion to 27 tons of blast furnace along the line was not affected, but indicators have improved markedly. Key words large ore batch, high coal rate, oxygen 1 引言 炼铁技术在近几年发展比较迅速，许多技术方面的问题、观点不一，相互之间很有必要学习，交流经验、 取长补短、提高操作、创造效益。 2 扩矿批、提煤比后的效果 2.1 实验过程 目前，多数450m3 系列高炉，据我所知矿批大多数都在 16～18t，随着炼铁原燃料价格的不断上涨，进 一步改善煤气利用，降低消耗提高指标，是摆在我们炼铁操作者面前的首要课题。在不锈钢公司 450m3 高 炉尝试了高煤比、大矿批。首先，450 高炉采用多环布料，矿批由 18t 扩到 25t ，随之扩到27t，高炉顺行没 有受到影响，指标反而得到明显好转。（1）综合燃料比下降20～30kg 。（2 ）煤气中CO2 提高 2%左右，炉顶 温度下降 50～80℃。（3 ）由于矿批扩大煤气流稳定，高炉可接受较高风压，热风压力由原来265kPa 增加到 285kPa ，冶强明显提高，日产增加约 50t。其次，在矿批扩大时，调整期煤比控制稍低（每吨铁 165kg/t）， 徐艳波，男，本科，wwwxyb031433@ 8-458 第八届（2011 ）中国钢铁年会论文集 待矿批扩大到 27t 后，炉况顺行未受影响，在炉温稳定，高炉顺行的基础上，减少焦批逐步提高煤比，增加 烟煤喷吹比例到 80%，煤比提高到吨铁 180kg 以上，高炉顺行条件比较好，能够在富氧率 1.5%～1.7%基础 上接受每吨铁 180～190kg/t 的高煤比。 2.2 高炉实现大矿批，高煤比要具备以下条件，采取相应措施 2.2.1 选择合理的炉顶布料方法 选择合理的炉顶布料方法，