钢包精炼渣系优化应用.pdfVIP

1钢包精炼渣系优化与应用 王建国 （湖南华菱湘潭钢铁集团有限公司, 湘潭 411101 ） 摘 要 钢包精炼渣系的选择和合适的渣成分组成，对实现快速造渣，改善精炼效果，缩短精炼时间，提高综合脱 硫效果和稳定钢中 Als 含量，降低精炼造渣成本，满足炉机匹配、生产节奏要求有着非常重要意义。湘钢宽厚板厂 根据品种钢开发、生产工艺要求，通过对不同钢包精炼渣系的选择并优化，有效地改善了 LF 精炼效果，提高了综 合脱硫效果，稳定了含铝钢生产，降低了精炼造渣成本，取得了较好的经济效益。 关键词 钢包精炼 渣系 优化 应用 Hot Metal Ladle Refining Slag System Optimization and Application Wang Jianguo (Hunan Valin Xiangsteel, Xiangtan, 411101) Abstract The hot metal ladle refining slag departments choice and the appropriate dregs ingredient composition, to realize the fast slag formation, the improvement fining effect, reduces the refining time, enhances synthesis desulphurization effect and in the stable steel the Als content, reduces the fining slag formation cost, satisfies the stove machine match, the production rhythm request to have the very important meaning.The Xianggang Generous Lumber yard basis variety steel development, the technique of production request, through and optimizes to the different hot metal ladle refining slag departments choice, improved the LF fining effect effectively, raised the comprehensive desulphurization efficiency, has stabilized including the aluminum steel production, reduced the fining slag formation cost, has obtained the good economic efficiency. Key words hot metal ladle fining, Slag system, optimization, application 1 引言 铝镇静钢—即终脱氧采用铝完全脱氧方式。一般成品钢中 Als 含量在 0.02%～0.05% 。铝在钢中具有 细化晶粒，改善钢材的冲击性能，提高时效性能，提高钢水纯净度，可将钢中的氧含量控制 20ppm 以下。 因此，铝及铝合金广泛用于特种钢、桥梁钢、船板、管线钢、高层建筑用钢、工具钢等专用钢种上。钢 包精炼渣系的选择和合适的渣成分组成对于铝镇静钢生产如何控制和稳定成品钢中 Als 含量，即在保证 成品材性能的前提下，又能尽量减少钢中夹杂物，控制夹杂物形态，改善钢水可浇性，提高铝收得率具 有非常重要意义。 在