Li4Ti5O12表面化学镀铜改善电池性能的探究.pdfVIP

第30届全国化学与物理电源学术年会 Li Ti O 表面化学镀铜改善电池性能的研究 4 5 12 王倩，刘微，张建，娄豫皖，夏保佳 （中国科学院上海微系统与信息技术研究所， 中国科学院大学 上海 200050 ；） 摘要：Li Ti O 表面化学镀铜后与 LiCoO 制得的 18650 电池，其倍率放电平台明显提高，并使得放电过程中的 4 5 12 2 温升明显降低。 关键词：锂离子电池； Li Ti O ；化学镀铜；温升 4 5 12 Study of the Batteries Performance of Li Ti O of Electroless 4 5 12 Copper Plating as anode materials Qian Wang，Wei Liu, Jian Zhang, Yu-wan Lou, Bao-jia Xia Department of Energy, Shanghai Institute of Microsystem and Information Technology, University of Chinese Academy of Sciences, Shanghai 200050, China Abstract: The Li Ti O /Cu composite was synthesized by electroless copper plating, and the 18650-type batteries 4 5 12 were assembled coupled with LiCoO2. The results showed that the discharging voltage plateaus were effectively improved, and the battery surface temperatures were also significantly decreased during the discharging process. Key Words: Lithium-ion battery; Li Ti O ; Electroless copper plating; Temperature. 4 5 12 尖晶石结构的钛酸锂（Li Ti O ）是锂离子电池负极材料之一，其理论容量为 175mAh/g，低于碳材料的 4 5 12 372mAh/g 。它具有比碳材料更正的嵌锂电位（1.55V vs. Li+/Li ），热力学上无锂枝晶生成；在脱嵌锂过程中晶格 常数几乎不发生变化，被称为“零应变”材料，表现出优异的可逆性和结构稳定性；用之制备的电池，具有循环 稳定性高、安全性好、充放电电压平稳等优点，主要应用于高安全、长寿命和高功率而对重量、体积比能量要 求不太高的场合[1] 。 钛酸锂本身的电导率仅约为 10-13S/cm，所以其电导率急需提高。通过制备工艺优化、掺杂、表面包碳等 方式均可提高其电子电导率，但都有一定局限性。本文在钛酸锂表面化学镀铜，并与 LiCoO2 制得 18650 电池， 对其倍率放电性能和电池表面温度进行了测定。 1、实验方法 将化学纯 EDTA·2Na、CuSO ·5H O、NaOH 依次溶解于去离子水中，磁力搅拌至完全溶解；再依次加入还原