不同精炼工艺对钢中夹杂物的影响.pdfVIP

不同精炼工艺对钢中夹杂物的影响 陈本文 栗 红 常桂华 杨 亮 （鞍钢股份有限公司技术中心，鞍山 114001） 摘 要 通过对比J55 石油套管钢采用LD-RH-LF-CC 和LD-LF-CC 两条工艺路线钢中氧、氮、氢及夹杂物的控制 水平，研究两条工艺路线钢中气体、夹杂物含量对产品性能的影响。试验结果表明：经两条精炼工艺处理后钢水及 铸坯的夹杂物是一致的，产品质量各项指标相同。因此从夹杂物角度考虑，采用LD-LF-CC 工艺可降低生产成本， 该研究为某些新钢种的工艺设计提供了理论依据。 关键词 J55 石油套管 真空冶炼 夹杂物 工艺设计 Effect of Different Refining Processes on Inclusions Chen Benwen Li Hong Chang Guihua Yang Liang （Ansteel Company Limited Technology Centre Anshan,114001 ） Abstract The levels of inclusions and gas content in molten steel and slabs of J55 grade oil casings were researched when adopting two processes: LD-RH-LF-CC and LD-LF-CC respectively. The purpose is mainly to research effect on inclusions and gas content in steel and mechanical properties of the final products through the two refining processes. The experimental results prove that inclusions content in molten steel and slabs and qualities of products are at the same level through the two refining processes. Furthermore, from inclusions aspect, the production cost can be cut down when adopting the process of LD-LF-CC. The research may offer theoretic foundations of process design to some new steel types. Key words J55 grade oil casings, vacuum refining, inclusions, process design 1 引言 目前油田使用的 J55 钢级油套管量占油套管总量的 60% ，J55 钢级是API5CT 标准中一个重要的钢 级[1] 。几年来，鞍钢在开发高级别J55 石油套管方面做了大量的研究工作，取得了宝贵的经验。但由于 生产工艺各个环节的不稳定因素，造成J55 油井管产生各种缺陷，这些缺陷一部分是轧制时造成的,一部 分是由连铸坯料带来的。分析研究夹杂物、气孔形成的原因并加以控制是十分必要的[2] 。本次试验通过 对比J55 石油套管钢采用LD-RH-LF-CC 和LD-LF-CC 两条工艺路线钢中氧、氮及夹杂物的控制水平 重点研究两条工艺路线钢水及铸坯中气体含量、夹杂物等变化，以此确定生产J55 石油套管钢最优生产 工艺路线，减少由夹杂物、气孔等原因所造成的产品缺陷，提高产品质量。本研究结果为今后某些钢种 的冶炼工艺设计提供技术依据。 2 试验条件 进行一个浇次 4 罐 J55 石油套管钢生产试验，试验工艺条件见表 1。两条工艺路线经LF 炉精炼处理合 金化后均进行喂 CaSi 线处理。 陈