Mn含量对一种高Ni低温钢性能的影响.pdfVIP

Mn 含量对一种高 Ni 低温钢性能的影响 1 2 1 朱莹光 董恩龙 侯家平 (1. 鞍钢股份有限公司技术中心，鞍山 114009 ；2. 鞍钢股份有限公司产品制造部，鞍山 114009) 摘 要 在一种高 Ni 低温钢中加入不同含量的 Mn，并采用QT 和 QLT 两种方式进行热处理，通过力学性能检验 和微观组织观察进行对比。结果显示，随 Mn 含量增加，晶粒逐渐细化，而强度与韧性均呈现先上升后下降的趋势。 与 QT 处理相比，QLT 处理后强度略有下降，而韧性则大幅提高，并出现明显的成分偏聚，偏聚随 Mn 含量升高而 加大，偏聚区的晶粒要比周围细小。 关键词 低温钢 QT QLT Effect of Mn Content on the Property of a Kind of High Ni Content Cryogenic steel Zhu Yingguang1 Dong Enlong2 Hou Jiaping1 (1. Technology Center of Angang Steel Company Limited, Anshan, 114001; 2. Product Department of Angang Steel Company Limited, Anshan, 114001 ) Abstract Different contents of Mn are added into a kind of high Ni content cryogenic steel, and two kinds of heat treatment regulations are employed, namely QT and QLT. The comparison items are property and structure. The results show that the crystal grains become thinner along with the increase of Mn content. At the same time, the strength and toughness increase at first, but fall when Mn content is too high. Comparing with QT treatment, the strength decreases a little after QLT treatment but the toughness improves greatly. Obvious segregation is gained after QLT, and it is enforced along with the increase of Mn content. The crystal grains within the segregation zone are thinner than other places. Key words cryogenic steel ，QT，QLT Ni 系低温钢的发展已经有七八十年的历史了，它的出现是对能源工业和现代工业的一大贡献。对于 Ni 系低温钢的技术要求一般是：在低温下具有足够的强度和韧性，具有良好的工艺性能、加工性能和耐腐蚀性 等[1，2] 。而合理的化学成分正是达到这一要求的关键之一。 Ni 系低温钢的成分相对简单，只有 C、Si、Mn 、Ni 。其中，Ni 含量是固定的，C、Si 含量因影响低温 韧性而受到严格限制，所以，只有 Mn 含量具有相对较大的可调空间。Mn 是置换式固溶强化元素，添加在 低温钢中可产生固溶强化，提高钢的强度，这是由于溶质原子（如 Mn ）固溶在钢的基体α—Fe 中，使溶剂 原子（Fe ）产生对称性的晶格畸变，其强化量的大小与溶质