邯钢炼铁部提高煤比生产实践 司俊朝 李志明 王婷婷 高 远 杨守慧 （邯钢炼铁部技术科） 摘 要 2010 年以来，炼铁部通过采取对外技术交流、创新操作制度、优化入炉燃料结构、提高风温、优化喷煤 工艺等措施，高炉不但保持了长期的稳定顺行，而且主要经济指标持续改善。从3 月起煤比连续达到150kg/t 以上， 从9 月起达到160kg/t，从10 月起连续两月165kg/t 以上。全年预计完成煤比155kg/t，与去年相比提高20kg/t 。 关键词 提高煤比 技术进步 生产实践 Producing Practise on Increasing Coal Rate in Ironmaking Department of Hansteel Si Junchao Li Zhiming Wang Tingting Gao Yuan Yang Shouhui (Ironmaking department of Handan Iron Steel Co., Ltd.) Abstract: Blast furnace not only has taken a long period of stability, but also made the major economic indicators continuously improving since 2010, throug operating system innovation, optimizing fuel structure and coal injection process, raising the wind temperature and foreign exchanges.Coal rate has being up to more than 150kg/t since March; it was up to 160kg/t in September and from October lasting two months it up to more than 165kg/t. Coal rate of 155kg/t a year is expected,which is 20kg/t more than last year. Key words increasing coal rate , technological improvement, producing practice 1 引言 近年来，随着邯钢加快淘汰落后工艺、产能，实现装备升级改造，邯钢高炉装备水平不断提高。1992 3 3 年，邯钢第一座1260m 高炉建成投产，2000 年，邯钢第一座2000m 高炉建成投产，2009 年5 月，邯钢东 区开始拆除4 座300 m3 级高炉，一次性淘汰落后产能170 万吨，2009 年7 月，随着3200m3 高炉建成投产， 邯钢炼铁部实现了高炉大型化、现代化。目前，炼铁部共有4 座高炉，1 座3200m3 级（8 号高炉），2 座2000m3 3 级（5 号和7 号高炉），1 座1000m 级（4 号高炉），具备年产生铁700 万吨的能力。 高炉装备的大型化不但客观上对原燃料的质量、设备管理水平、生产组织提出了更高的要求，而且也需 要高炉操作理念不断创新，操作技术不断进步，以适应高炉的大型化需求。 针对上述情况，2010 年以来，炼铁部通过采取对外技术交流、创新操作制度、优化入炉燃料结构、提 高风温、优化喷煤工艺等措施，高炉不但保持了长期的稳定顺行，而且主要经济指标持续改善。从3 月起煤 比连续达到150kg/t 以上，从9 月起达到160kg/t，从10 月起连续两月165kg/t 以上。全年