Q450NQR1 高耐候板氧化铁皮除鳞控制 杨安林 (攀钢集团攀枝花钢钒有限公司热轧板厂，攀枝花 617062) 摘 要 结合攀钢热轧板厂加热炉生产工艺，通过优化 Q450NQR1 高耐候板坯的不同装炉温度及规格下的加热工 艺制度等，提高了板坯炉生氧化铁皮去除效果，炉生氧化铁皮除鳞合格率（达到 2 级）为 92.6% 。同时为其他系列 的高耐候板坯加热工艺改进提供依据。 关键词 高耐候板坯 炉生氧化铁皮 除鳞 The Controlling of the Scale Breaking of Q450NQR1 the Corrosion Resistance Steel Slab Yang Anlin (PanGang Group Panzhihua Steel ＆ Vanadium Co.,Ltd.,Panzhihua, 617062) Abstract According to the reheating production technics of the of Pangang hot strip mill ,through optimizing the reheating system of dissimilar charging temperature and dissimilar dimension to the Q450NQR1(the corrosion resistance steel slab ）. Raised remove results of the scale breaking,and the percent of pass to scale by furnace breaking is 92.6%.And produce basis for the improving reheating production technics of the other corrosion resistance steel. Key words the corrosion resistance strip, the scale by the furnace, break scale 1 引言 热轧板厂现有两座大型步进梁式板坯加热炉，主要加热一般碳素结构钢、优质碳素结构钢、冷轧用低碳 钢和低合金钢等钢种，其中 Q450NQR1 高耐候板坯用于生产铁道货车用高强度耐大气腐蚀钢板。板坯在加 热过程中，因炉气中含有大量 CO [1] 、H O 和过剩 O 等氧化性气体，钢的表层发生氧化形成炉生氧化铁皮 。 2 2 2 一般炉生氧化铁皮经高压水除鳞后都能去除干净，但以 Q450NQR1 为代表的高耐候系列板坯出炉除鳞后存 在除鳞不净现象，除鳞合格率仅 80％左右，板坯表面局部或大面积有炉生氧化铁皮。若轧制前不能完全去 除炉生氧化铁皮，轧制过程中将其压入带钢表面，将会产生板卷表面氧化铁皮压入质量缺陷，严重时影响产 品的机械性能，还会劣化轧制状态，甚至出现废钢或损坏主轧线设备。 2 Q450NQR1 高耐候板坯除鳞缺陷及成品红锈成因 Q450NQR1 高耐候板坯经 E1R1 前除鳞箱除鳞后，板坯表面出现白雾、残留片状或沟壑状未除尽的炉生 氧化铁皮，进而影响产品表面质量。相同工艺控制情况下，2 号加热炉除鳞不尽的比率高于 1 号加热炉，一 般头部除鳞好于尾部。按炉生氧化铁皮除鳞效果的残留程度级别，达到 2 级的高耐候板坯炉生氧化铁皮除鳞 [2] 合格率仅为 80%。从而使成品钢卷