宝钢减少异钢种连浇插铁板研究.pdfVIP

宝钢减少异钢种连浇插铁板研究 董金刚1 （宝山钢铁股份公司制造管理部，上海 201900 ） 摘 要 为了提高连铸生产能力、减少不同成分牌号钢种的混钢量，宝钢在 1930mm 连铸采用了插铁板生产工 艺，插铁板也带来了板坯切割损失和质量不稳定等问题。在分析插铁板原因基础上，通过采取连浇规程的优化完 善、钢种牌号和保护渣的匹配优化以及生产组织的优化等措施，插铁板次数下降了 20% ，减少了板坯报废，提 高了板坯价值。 关键词 异钢种 连铸 插铁板 生产能力 保护渣 Research on Decreasing of Inserting Metal Plate during Different Steel Grades Continuous Casting in Baosteel Dong Jingang （Baosteel Manufacture Department, Shanghai, 201900 ） Abstract In order to increase capacility of continuous casting and decrease mixing molten steels of different grades， inserting metal plate process has been used in Baosteel 1930mm casting machines，but inserting metal plate caused the slabs cutting loss and quality non-stability，Based on analyzing the inserting metal plate causes，the measures have been taken which are optimal continuous casting regulations，matching grades and powders，improving production arrangement， inserting metal plate has been cut 20%，slab loss was decreased，slab values was increased. Key words different steel grades, continuous casting, inserting metal plate, capacility, powder 1 引言 受钢种多、批量小和交货周期严等因素的影响，为提高连铸生产的连续性，扩大 CAST 连浇炉数，宝 钢1930mm 连铸采用了插铁板的生产方式，其中1CC 为自动插铁板，2CC 为手动插铁板。插铁板在提高连 铸生产能力的同时也带来不利影响，体现为板坯在插铁板附近取样而造成切割损失、拉速波动造成板坯质量 不稳定、插铁板前后拉速升降造成产能损失，因此需要考虑在扩大生产连续性的同时降低插铁板次数。 2 设备和工艺简介 宝钢总部共有6 台板坯连铸机，分布在一、二两个炼钢生产单元，其中一炼钢生产单元的主要设备有： 3×300t 转炉、3 台RH 、2 台LF、3 台CAS、2 台1930mm 连铸机、1 台2300mm 连铸机。2 台1930mm 连铸 机采用塞棒和滑板控制钢流，具有插铁板功能，可满足在成分差异大的不同钢种之间连浇。 插铁板包括同一中间包内不同钢种连浇插铁板（简称包内插铁板）和中间包交换时不同钢种连浇插铁板 （简称换包插铁板）。包内插铁板是指同类别保护渣的不同钢种之间连浇的情况，换包插铁板主要针对不同类 别保护渣的异钢种连浇的情况。包内插铁板比例为65%左右，70%的插铁板发生在1CC。 1董金刚，男，硕士，高级工程师，从事生产管理和质量管理，dongjingang@ 8-2 第八届（2011 ）中国钢铁年会论文集 3 插铁板的原因 插铁板的根本原因是为了满足成分差异大的不同钢种之间实现连续生产的同时减少混钢，提高连铸生产 能力，降低生产成本