MBR 矿热风烧结实验研究 1 1 2 1 邵 帅 何志军 金永龙 张军红 （1．辽宁科技大学，鞍山 114051 ；2 ．唐山钢铁集团有限责任公司，唐山 063016 ） 摘 要 烧结过程的余热利用是钢铁工业的一个重要课题，而热风烧结是烧结余热利用的一种重要方式。本文在实 验室条件下，进行了MBR 矿热风烧结研究。结果表明在适宜的热风温度和供热风条件下，热风烧结可以提高烧结 矿的转鼓强度和提高烧结速度，同时增加烧结矿中冶金性能良好的铁酸钙含量。 关键词 热风 烧结 MBR 矿 Hot Air Sintering Experiment Research of MBR Ore Shao Shuai1 He Zhijun1 Jin Yonglong2 Zhang Junhong1 (1 ．University of the Science and Technology Liaoning ，Anshan ，114051; 2 ．Tangshan Iron Steel Group Co.,Ltd., Tangshan，063016) Abstract The sintering process of waste heat utilization was an important subject of steel industry, and hot air sintering waste heat utilization of sintering was a kind of important ways. Based on the laboratory scale conditions, hot air sintering experiment of MBR ore was researched. The results indicated that the hot air sintering could improve sinter strength and change sintering speed under the appropriate condition of the hot air temperature and supply time of hot air. And the lath-shape calcium ferrite which can enhance the good metallurgical property of the sinter were increased. Key words hot air, sintering, MBR ore 1 引言 烧结过程的余热利用是钢铁工业的一个重要课题。在烧结工序中有 50 ％左右的热能被烧结烟气和冷却 机废气带走[1] 。目前，国内对于烧结余热的回收利用主要有发电、热风烧结、热风点火、预热物料及利用余 热锅炉回收生产蒸汽等方式。据有关数据统计，我国烧结工序余热利用率目前不足 50 ％，与发达国家相比 差距较大，导致每吨烧结矿的平均能耗要比发达国家高 15kg 标煤左右[2] 。这表明国内各冶金企业在合理应 用烧结余热方面还大有潜力可挖。目前，我国烧结余热利用主要是利用热筛上烧结矿余热和环冷机废气余热 来生产蒸汽[3] [4] 。此外，利用热风烧结是烧结余热利用的另外一种重要方式 。根据烧结理论，热风烧结时， 由于热风能够补偿烧结料层上部热量的不足，提高上层烧结矿温度，并减缓上层烧结矿的冷却速度，减少上 下料层的温差，使上层烧结矿强度增加，上、下层烧结矿质量差别减小，从而达到提高烧结成品率的目的。 另外，热风烧结可相应地减少固体燃料消耗，节约能源，改善烧结气氛，提高烧结过程氧位，减少局部过熔 现象，降低烧结矿中FeO 含量，改善烧结矿还原性能。 何志军，男，硕士，讲师，从事冶金过程资源与环保，hzhj2002@126