改善厚料层烧结透气性的试验研究 贺淑珍 周 昊 （山西太钢不锈钢股份（有限）公司，太原 030003 ） 摘 要 针对 700mm 以上的高料层烧结过程中，出现烧结过程料层透气性恶化的问题，在太钢技术中心进行了采 用支撑板改善烧结过程料层透气性的烧结杯试验研究。试验结果表明：采用 350mm 高度支架支撑作用效果最好， 料层收缩显著降低，利用系数提高了 15.2％，转鼓强度保持原有水平，烧结矿冶金性能改善。进而进行了工业性生 产试验，台车料面收缩显著减少，垂直烧结速度加快，生料层减薄，取得了很好的效果。 关键词 高料层烧结 支撑板 烧结过程透气性 产量1 Experimental Study on Improvement in Permeability Sintering Process for TISCO He Shuzhen Zhou Hao （Technology Center of Taiyuan Iron and Steel (Group )Co., Ltd.，Taiyuan, 030003 ） Abstract Aimed to solving the problem that permeability in sintering process worsens while the bed of material is above 700mm,in this paper, a new technology-supporting sintering process was presented. The influence of stand-support and its height on technico-economic-indices were also studied under laboratory condition. The results showed that applying 350mm stand-support was best,and the bed shrinkage was decreased obviously,the productivity increased by maximum 15.2 ％and the drum index retained former level，the metallurgical properties of sinter were improved. Key words deep bed sintering, stand-support, permeability in sintering process, productivity 烧结过程的透气性包括原始料层透气性和烧结过程透气性，原始料层透气性与混合料粒度组成和混合料 水分有较大的关系，而烧结过程透气性与烧结过程矿物的反应性、液相生成、上部烧结饼的荷重作用有关系。 原始料层透气性可以通过强化制粒、改善原燃料粒度组成、控制合理水分含量、混合料预热、在烧结料中混 入大的颗粒等手段来得到改善。烧结过程透气性的改善，除了优化烧结配矿结构外，还要借助于外部手段的 实施，以控制和减轻烧结矿层的荷重。国外进行了许多研究，提出了包括采用物理场(磁力)和机械力(支撑板) 等多种解决方案。由于磁力悬浮烧结法需要对烧结设备进行大的改造，未进行工业生产化，而日本君津厂将 支撑烧结法用于烧结面积为 500m2 的烧结机上，取得了生产率提高 10％，成品率和烧结矿转鼓强度几乎不 变的效果。 太钢烧结料层厚度为 700mm 左右，为了改善烧结过程料层透气性，提高烧结矿产量，实验室进行了应 用支撑烧结技术的试验研究。 贺淑珍（1968-），女，大学本科，教授级高工，hesz@ 改善厚料层烧结透气性的试验研究 8-129 1 实验条件 1.1 烧结配料比及烧结参数 烧结原料取自于太钢生产现场，配矿方案