焊后热处理对钛合金电子束焊接接头残余应力分布的影响.pdfVIP

HotWorkingTechnology2019,Vol.48,No.l7

焊后热处理对钛合金电子束焊接接头

残余应力分布的影响

李立峰，黎刚刚，马天驹，张静

(兰州空间技术物理研究所压力容器事业部，甘肃兰州730000)

摘要：采用StresstechXRD3000型X射线衍射仪检测了真空热处理前后TC4钛合金电子束焊接接头的残余应

力分布情况。结果表明.真空热处理对焊接接头的残余应力分布有重要影响，采用适当热处理工艺参数可大大降低残余

应力。-

关键词：TC4钛合金；真空热处理；残余应力

DOI:10.14158/j.cnki.1001-3814.2019.17.040

中图分类号：TG441.8文献标识码：A文章编号:1001-3814(2019)17-0154-04

EffectofPost-weldHeatTreatmentonResidualStressDistribution

ofElectronBeamWeldedJointsofTitaniumAlloy

LILifeng,LIGanggang,MATianju,ZHANGJing

(PressureVesselBusinessDivision,LanzhouInstituteofPhysics,CAST,Lanzhou730000,China)

Abstract:TheStresstechXRD3000X-raydiffractometerwasusedtodetecttheresidualstressdistributionofelectron

beamweldedjointsofTC4titaniumalloybeforeandaftervacuumheattreatment.Theresultshowthatvacuumheattreatment

hasanimportantinfluenceonthedistributionofresidualstressofweldedjoint,andtheresidualstresscanbereducedgreatly

byusingappropriateheattreatmentparameters.

Keywords：TC4titaniumalloy;vacuumheattreatment;residualstress

贮箱是各种推进系统最重要的部件之一，所用力凹。因此，在贮箱赤道缝电子束焊接后，为了减少

的母材为钛合金，其作用是给发动机提供脐、N2O4残余应力的影响，必须采用热处理的工艺措施㈣。目

等推进剂工作介质。贮箱赤道焊缝是贮箱的最主要前,还没有对真空热处理前后焊缝附近残余应力的分

承力焊缝，所以赤道焊缝的焊接是贮箱满足设计要布情况进行过研究，没有对真空热处理对电子束焊接

求的关键技术冋。接头残余应力分布的影响程度进行过分析和评

钛及钛合金由于比强度高、抗腐蚀性好、高温工价叶叫因此，本文选用了最常见的TC4钛合金作为

作性较好以及高塑性等优点，被压力容器行业广泛研究对象,对贮箱赤道缝电子束焊接模拟试件热处理

采用切。电子束焊接(electronbeamwelding,EBW)是前后的残余应力进行了检测；分析了真空热处理前后

三种高能量焊接方法之一，具有能量密度