TRT发电机静叶承压缸叶片修复工艺.docxVIP

TRT 发电机静叶承压缸叶片修复工艺米晋斌 1 TRT 发电机静叶承压缸叶片修复工艺 （1 太原钢铁集团有限公司; 2 山西省电力建设四公司,山西太原,030012） 【摘 要】介绍了马氏体不锈钢 1Cr13Mo 叶片补焊工艺，根据厂里要求修复后要达到的效果、马氏体不锈 钢的特性、叶片磨损程度和工期要求合理制定焊接修复工艺，圆满完成叶片修复工作，目前机组运行正常。 【关键词】马氏体不锈钢;叶片;焊接修复 【中图分类号】 TM61 【文献标识码】 B 【文章编号】1006-6764（2014）08-0068-03 DOI:10.13589/j.cnki.yjdl.2014.08.020 Repair Process for the Blades of Stationary Blade Bearing Cylinder of TRT Generator Mi Jinbin1, Wang Shiqiang2 (1. Taiyuan Iron and Steel (Group) Co., Ltd.; 2. Shanxi Electric Power Construction Company, Taiyuan, Shanxi 030012, China) [Abstract] The repair welding process for the 1Cr13Mo blades of martensite stainless steel was introduced. Repair welding process was properly designed according to the repair requirement, the characteristics of martensite stainless steel, wearing degree of the blades and time limit of the work. The blades repair work was successfully completed and the unit has been normally operating since. [Key words] martensite stainless steel; blade; repair welding 1 概述 太原钢铁（集团）有限公司厂内 TRT 发电机组 静叶片磨损严重，影响到机组运行，需要进行补焊修 复。TRT 是利用高炉炉顶煤气中的压力能及热能经 透平膨胀做功来驱动发电机发电。静叶承压缸共有 两级静叶，一级静叶为可调式静叶，控制气体流量， 调节机组参数；二级静叶为固定静叶，起导流作用， 让气体沿轴向均匀对汽轮机做功。为了能够保质保 量按期完成静叶片的补焊工作，让机组尽快投入生 产，我们制定了修复工艺。磨损叶片见图 1 和图 2。 图 1 一级叶片磨损图  图 2 二级叶片磨损图 2 修复后要达到的效果 2.1 修复后的叶片不能断裂，在运行中如果叶片断 裂，会给高速运转的机组造成更大损伤。TRT 作为 高炉的附属设备，对高炉的生产有着重要的作用，因 此 TRT 的运行必须以保证高炉正常运行为前提，不 允许对炉况产生不良影响。 2.2 修复后的叶片强度满足运行要求，由于高炉煤 气中有灰尘，叶片易磨损，气体中含腐蚀性的氯和二 氧化硫等物质，溶于水后形成酸对叶片造成腐蚀。 2.3 修复后的叶片能满足运行时间要求，厂内在检 修时已经对磨损叶片进行了订货，所以此次修复后 2014 年第 8 期 总 第 174 期 冶 金 动 力 METALLURGICAL POWER 69 的叶片保证在备件回来之前安全稳定运行，不出现 质量问题。 3 叶片材质性能和修复难点分析 静叶片的材质为 1Cr13Mo，为比 1Cr13 耐蚀性 高的高强度马氏体不锈钢，由于其塑性和韧性很差， 焊接时有强烈的淬硬和冷裂倾向，焊接后残余应力 大，易产生裂纹。 焊接时需要采取焊前预热，控制层间温度，焊后 缓冷等工艺措施。1Cr13Mo 化学成分和性能见表 1。 表 1 1Cr13Mo 化学成分主性能 化学成分 C Si Mn S P Cr Mo 0.08~0.18 ≤0.60 ≤1.00 ≤0.030 ≤0.035 11.50~14.00 0.30~0.60 淬火回水状态下 1Cr13Mo 性能 抗拉强度（MPa) ≥685 伸长率 A（%） ≥20 断面收缩率 ψ (％) ≥60 硬度 ≥192HB 本次共有 1 级静叶 6 片、2 级静叶 22 片需要补 焊，钢材的特殊焊接性、严格的焊接工艺执行、工作 量大、工期紧张成为了我们的修复难点。 4 焊材选用 1C