试验用钢在zg.doc

稀土Ce-La对SS400钢晶粒度及夹杂物变性的影响 杨吉春，聂亚丽左立杰赵丙新 （内蒙古科技大学 材料与冶金学院内蒙古包头 014010） 摘要：对SS400钢进行了添加稀土Ce-La合金的试验研究。采用光学显微镜和扫描电镜（SEM）观察和分析钢的晶粒度和夹杂物成分及形貌。结果表明加入稀土后晶粒度提高了1~2级；加入0.05%的稀土Ce-La硅酸盐夹杂物近似椭圆形加入量达到0.09%时，硫化物夹杂和硅酸盐夹杂均呈圆形。 关键词：钢Ce-La合金；晶粒度；夹杂物Effects of Rare Earth Element Ce-La on Grain Size and Inclusion Modification of SS400 Steel YANG Ji-chun, NIE Ya-li, ZUO Li-jie, ZHAO Bing-xin (School of Materials and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010, Inner Mongolia, China) Abstract：Th experimental study of adding rare earth Ce-La alloy in SS400 steel was conducted. The grain size, composition and microstructure of inclusion were observed and analyzed in steel with optical microscope and scanning electron microscope (SEM). The results show that grain size of steel enhances 1~2 levels after adding the rare earth; the silicate inclusion is approximate ellipse with 0.05% addition of rare earth Ce-La, furthermore, the sulfide and silicate inclusion are circular shape when the addition of rare earth Ce-La reaches 0.09%. Key words：steel; Ce-La alloy; grain size; modification of inclusion SS400是一种普通结构用钢，大量应用于建筑及工程结构。近几年来，在车辆、船舶、桥梁等领域的应用越来越广，品种日趋多样化。通过获得均匀的细晶使SS400钢具有优良的综合力学性能。有文献报道(1(，稀土元素在钢中起到改善夹杂物形态、细化晶粒的作用。本文通过加入不同量的稀土，分析稀土对SS400钢的晶粒度及夹杂物成分、形态和尺寸的改变，从而改善钢的性能。 1 试验料及方法 1.1 试验在ZG-0.01真空中频感应炉中冶炼SS400钢浇注成4.0g的锭C 0.04~0.08、Si 0.14、Mn 0.40、P 0.08、S 0.06、Fe余。稀土Ce-La混合细丝的加入，2#钢锭稀土加入量为0.05%，3#钢锭稀土加入量为0.09%。将浇注后的钢锭经1 100 ℃加热锻造25 mm(25 mm的方坯。 1.2试验方法 从锻造坯横向（垂直于锻轧方向）截取抛光面为10 mm(10 mm的金相试样，砂纸粗磨抛布抛光后用4%的硝酸酒精腐蚀，进行晶粒度评定。从锻造坯纵向（平行于锻轧方向）截取抛光面为20 mm(10 mm的金相试样，经粗磨、细磨、抛光后，进行夹杂物观察。 2试验结果及讨论 2.1稀土对晶粒度的影响 收稿日期：2012-03-14 基金项目：国家自然科学基金内蒙古自然科学基金重点项目（2010Zd105）；内蒙古高校项目(NJ2207098)作者简介：杨吉春（1963），男，博士，教授，硕士生导师. 图的(a) 0%;(b) 0.05%;(c) 0.09% Fig.1 Microstructure of SS400 steel with different addition of Ce-La alloy: (a) 0%; (b) 0.05%; (c) 0.09% 采用将试验钢的晶相图与GB-6394-2002标准金属平均晶粒度测定图谱进行对比评定试样晶粒度。未加稀土SS400钢的晶粒度为7级，加入0.05%稀土是8~8.5级，提高了1~1.5级。稀土加入量为0.09%的SS400试验钢晶粒度