内蒙蒙东褐煤制备活性焦的试验研究-中国大唐集团公司.PDFVIP

2014 论文汇编 内蒙蒙东褐煤制备活性焦的试验研究 宋学平 （大唐国际化工技术研究院有限公司 ） 摘 要：以内蒙蒙东褐煤为原料，在活性焦制备小试试验装置上，以水蒸气为活化介质，用 正交试验方法考察了活化温度、活化时间、水蒸气流量对活性焦产品的碘吸附值、亚甲基蓝 吸附值及收率的影响。结果表明，综合考虑活性焦的亚甲基蓝吸附值及收率的影响，最佳的 活化条件为：活化温度 800℃，活化时间为 90min，水蒸气流量 2g/min，在最佳工艺条件下 所制得的活性焦中孔发达，中孔孔径在4.0nm 附近分布比较集中。 关键词：褐煤；活性焦；中孔 [Abstract] This paper presented the preparation of activated coke from Inner Mongolia East Mongolia lignite, The activation reactions were studied using the tubular electro-thermal furnace with water stream as activation gas. The orthogonal experiments, in which the activation conditions were activation temperature, activation time and vapor velocity, were carried out to inspect the effects of reaction conditions on activated coke properties. The result shows that the optimum activation conditions were determined as: activation temperature 800℃, activation time 90min and vapor velocity 2g/min, with comprehensively consideration of methylene blue adsorption value and yield rate. The sample which was prepared under the optimum condition had a developed mesopore with a diameter of 4nm. [Keywords] Lignite; Activated coke; Mesopore 1 引言 活性炭广泛应用于废气、废水的处理[1,2] ，但较高的价格严重限制着其应用。褐煤基活 性焦是一种以褐煤为原料，经过炭化和活化过程而制得的一种多孔的含碳物质，是没有得到 [3] 充分干馏或活化的煤基活性炭类吸附剂 。与活性炭相比，褐煤基活性焦不仅具有活性炭的 相关特性，而且价格更加低廉，近年来褐煤基活性焦在废气、废水处理中的应用已经受到广 泛关注[4,5] 。本文以我国内蒙蒙东某煤矿的褐煤为原料，以水蒸气为活化剂，采用正交试验 方法考察了活化温度、活化时间、活化剂 （水蒸气）流量对褐煤基活性焦样品吸附性能的影 响，为褐煤基活性焦生产提供借鉴和参考。 2 实验部分 2.1 实验原料 实验所用褐煤取自内蒙古蒙东某煤矿，褐煤的工业分析和元素分析见表 2- 1。 81