上流型反应器中光催化剂处理印染废水研 摘要试验采用铁铈共掺杂的TiO2光催化剂在周围管布置上流型光催化反应器中处理人造丝织物印染废水。达到了充分发挥TiO2光催化剂的催化性能的目的，并解决了催化剂与水分离的主要问题。试验结果表明在上流型反应器中加入10g/L双元素掺杂改性的TiO2光催化剂，曝气量0.5m3/L，处理水样240min后出水水质色度去除率，COD去除率去除效果良好。 关键词 印染废水； 复合掺杂； 上流型； 光催化氧化 Abstract：Experiment with Fe3+-Ce4+-doped dual-element modified TiO2 photocatalyst in self-made upper edge light-type photocatalytic reactor to deal with man-made silk fabric printing and dyeing wastewater. The successful solution of a catalyst and water separation, while achieving a full play of the pairs of elements in the performance of modified TiO2 photocatalyst purposes. The results showed that: carrier calcination temperature, PH, reaction time and other indicators affect the photocatalytic effect. In the upper-type reactor by adding 10g/LFe3+-Ce4+ pairs of elements of doped TiO2 photocatalyst, aeration 0.5m3 / L, treated water samples after 240min water quality color removal efficiency of 97.4%, COD removal rate was 73.8%, remove good effect. Key words ：Printing and dyeing wastewater; co-doped; upper edge light type; photo catalytic oxidation; pairs of elements 中图分类号：TU74文献标识码：A 文章编号： 对印染废水的处理研究，光催化反应器是该研究领域的一个重要的课题。它性能的好坏直接决定着光催化效率的高低，同时也是光催化剂的回收的关键因素 [1-2]。目前，对于光催化反应器的研究主要集中在悬浮型光催化反应器，其主要针对纳米TiO2粉体[3-4]。应用这种反应器结构比较简单，但存在后续处理必须经过过滤、离心、絮凝等一系列的方法将其分离并回收，使得过程较复杂。而负载型光催化反应器不存在着后续处理问题，并可以连续化处理。 本试验采用自行设计制造的上流型光催化反应器来克服传统的负载型反应器的弊端。使其具有接触面积更大、分离更容易的优点，并且大幅度提升了光利用率高，有效的避免了阻塞等问题的出现。试验采用双元素掺杂的TiO2光催化剂，降解印染废水水样。探讨影响上流型光催化反应效果的因素。 1 实验部分 1.1试验水样 水样取自沈阳某丝织物印染厂，其废水性质经检测 COD稳定在450mg／L，可生化性差，pH值7～8，色度200倍。 1.2催化剂制备 本实验的催化剂采用溶胶-凝胶法制备。在B溶液中掺杂0.5%Fe3+-0.1% Ce4+双元素制得TiO2光催化剂，形成均匀透明橙黄色TiO2溶液，陈化24h形成含有掺杂离子的TiO2溶胶，装入磨口玻璃瓶中待用。 将烘干洗净的粗孔硅胶微球浸入上述制备好的TiO2溶胶中30min，使其均匀负载，取出后在电热烘干箱内恒温135℃烘干2h，然后再放在马弗炉中450℃焙烧 4h，即制得光催化剂。 1.3 试验装置 本试验所用装置是以三相体系为研究对象来设计光催化反应器。设计反应器利用紫外线杀菌灯为光源的环状玻璃反应器，顶端开口、底部设有多孔曝气系统。 1.4水质分析方法 印染废水的COD、浊度、色度值分别按国标GB 11914-1989， GB 11903-89， GB 13200-91进行测定。 2 结果与讨论 2.1 催化剂投加量对降解印染废水的影响 取水样2.5L调节pH=3，