盐雾环境下钢筋混凝土的阴极保护 何小松 1 赵娟 2 （1 东方建设（天津）防腐工程有限公司，天津，3000457 2 赵娟 中交第一航务勘察设计院 300222） 摘要：本文主要介绍盐雾环境下钢筋混凝土锈蚀的基本原理.混凝土外加电流阴极保护 的设计、实施及调试的要点。混凝土外加电流阴极保护是一项极其复杂的工作， 在设计、安装过程中要充分考虑到各种因素对系统的影响。在安装过程中随时 要检测如电连接，阴阳极的绝缘。系统的判断准则一般多用 100mV 衰减，而不 是我们一般港工钢结构阴极保护的保护范围原则。 关键词: 盐雾 混凝土 腐蚀 阴极保护 Cathodic Protection of Steel in Concrete in Salt Atmosphere He, Xiao-song (Orient (Tianjin) corrosion Engineering Ltd) Abstract: It is mainly introducing the principle of the corrosion of steel in concrete which be confronted with salt atmosphere. The key point such as design ,installing and commission must be consider.。Cathodic protection of steel in concrete is a very complicated work ,we must take care of every detail which could result in the failure of the system. Detections such as electrical continuity ,the insulativity between the anode anode cathode would be done during the installing process. A representative point of meet the potential decay over a maximum 24h at least 100mv from instant off often be used as the criteria of concrete cp system ,it is differ from the cathodic protection of marine steel structures. Key words: Salt Atmosphere concrete corrosion cathodic protection 一、钢筋锈蚀的危害性 混凝土耐久性是当今世界的大问题，钢筋混凝土结构是目前工程的主要结构 形式。有关文献报道当今世界混凝土破坏原因，按递减顺序是：钢筋腐蚀、冻 (1) 害、物理化学作用。 文章明确地将钢筋腐蚀排在影响混凝土耐久性因素的首 位。而来自海洋环境的氯盐和用于化冰雪的除冰盐，又是造成钢筋腐蚀的主要原 因。美国 1984 年报道，仅就桥梁而言，57.5 万座钢筋混凝土桥，一半以上出现 钢筋腐蚀破坏，40%承载力不足和必须修复与加固处理，当年的修复费为 54 亿 美元；1988 年报道，钢筋混凝土腐蚀破坏的修复费，一年要 2