含磷高强IF钢热轧轧裂原因分析.pdfVIP

含磷高强 IF钢热轧轧裂原因分析 王 畅 于 洋 刘 珂 王 林 陈 瑾 焦会利 (首钢技术研究院) (首钢股份公司迁安钢铁公司) 摘 要 观察了含磷高强 IF钢热轧轧裂缺陷的微观形貌及热轧卷拉伸试样断口情况，分析了轧裂形成原因 主要始于连铸坯的中心偏析造成的中部裂纹及中部缩孔等内部缺陷。根据现有连铸工艺条件提出了控制过 热度低于3O℃ 以及加大轻压下量至4mm等改善措施，可有效改善连铸坯内部质量，减轻中心裂纹及缩孔 的产生。 关键词 热轧 含磷高强 IF钢 中心偏析 轻压下 过热度 Research ofRollingCrackofHotRolledP—Added High StrengthIF Steel WANG Chang。 YUYang LIUKe WANGLin CHENJin JIAOHuili (ShougangResearchInstituteofTechnology) (ShougangQiananIronSteelCompany) Abstract Themicrostructureofrollingcrackdefectandthefractureoftensilesampleofthehot rolledP—addedhigh strengthIFsteelwereobserved．Thereasonsforrollingcrackwereanalyzed， which showed that inner defects such as middle fissure and shrinkage resulting from center segregationofcontinuouscastingslabwasthemaincause．Accordingtocurrentcontinuouscasting process，improvementmeasures，including controlling the superheatto lower than 30 ℃ and increasingsoftreductionamountto4mm wereputforward，which couldeffectivelyimproveinner qualityoftheslabandreducethemiddlefissureandshrinkagedefects． KeyWords hotrolling，P-addedhighstrengthIFsteel，centersergegation，softreduction，superheat 冷轧高强超深冲钢板的特点是采用超低碳成 本文通过试验分析发现，热轧过程中的轧裂 分设计，通过铌和钛固定碳和氮等间隙原子形成 原因与连铸过程中磷的中心偏析造成的中心裂纹 无间隙原子钢 (IF钢)，通过添加磷、锰、铜和 和中心缩孔密切相关。早期采用低过热度增加等 硅等固溶强化元素进行强化，在保持带钢 良好深 轴晶抑制凝固末期富含杂质钢水向中心流动来减 冲或超深冲性能的同时，可使钢板的抗拉强度提 轻中心偏析 J，后来 日本钢管公司 (NKK)为了 高到440MPa级或更高级别，可用于汽车外板成 生产抗 HIC (氢诱发裂纹)管线钢开发了静态 形件或较复杂的内板成形件的生产。其中，磷作 轻压下技术，并利用其减小中心偏析 J。根据朱 为常用的强化元素，在高强 IF钢的生产中起着 苗勇等人的研究，轻压下技术是通过在凝固末端 重要的作用。磷有助于提高钢的强度，但是由于 适时施加一定的压下量来补偿凝固后期钢水的凝 磷的中心偏聚特性，磷含量的增加会恶化钢的机 固收缩，减少浓化钢水的横向流动，同时抑制富 械性能，导致连铸坯内部中心裂纹、中心缩孔及 集溶质在中心聚集，减小中心偏析 J。轻压下技 板卷分层等情况。如