离心铸造原位Mg2SiAl复合材料的组织控制.PDFVIP

2 0 0 9 中国铸造活动周论文集 离心铸造原位Mg Si/Al 复合材料的组织控制 2 妞，刘 雁，赵宇光 （吉林大学材料与工程学院，长春 130025 ） 摘要：采用离心铸造法制备了初生Mg Si 相偏聚于内层呈梯度分布的颗粒局部增强铝基复合材料， 2 研究了Mg Si/Al基复合材料的组织形态，以及P变质处理和铸型转速对其的影响。结果表明：0.5wt.% 2 磷变质可明显细化复合材料 的初生Mg Si 相，组织形貌由粗大的枝晶状变为细小的多边形；随着 2 铸型转速的提高，梯度分布越明显，初生Mg Si 组织越细化。 2 关键词：离心铸造;MgSi/Al 基梯度复合材料;组织形貌 2 Abstract ：The centrifugal casting was used to produce particle reinforced locally Al matrix composites exhibiting Mg Si particulates reinforcement in inside wall. The microstructure of Mg Si/Al gradient 2 2 composites, the effect of phosphor and the mould velocity on the morphology and distribution of Mg Si/Al gradient composites were researched. We found that 0.5 wt.% phosphor can modify the primary 2 Mg Si from dendrite to small polygonal; with the increase of the mould velocity, graded distribution was 2 more evident, the primary Mg Si was finer. 2 Key words: the centrifugal casting; Mg Si/Al gradient composites; the morphology 2 1 引言 随着轨道交 和汽车工业的高速发展，能源紧缺、环境污染等问题日益严重，以减重节能为目 3 -3 标的车辆轻量化技术研究开发备受关注。由于Mg Si 具有高熔点（1085℃），低密度（1.99×10 kg m ）， 2 9 -2 -6 -1 高硬度 （4.5×10N m ），低热膨胀系数（TEC）（7.5×10 K ）和高的弹性模量（120GPa），与基体 相容性好,界面干净,结合牢固，热稳定性好，增强体分布均匀，同时制造工艺简单、成本低廉的优 点，Mg Si/Al 复合材料受到越来越多的关注。然而，初生Mg Si 一般