甘肃老金厂金矿北金矿区矿石难浸原因研究-中国选矿选煤网.docVIP

甘肃老金厂金矿北金矿区矿石难浸原因研究 杜世勇(1．甘肃有色宝纳矿业有限公司；2．甘肃有色地质勘查局四队) 摘要从北金矿区矿石性质手，结合实际生产的情况，重点分析了北金金矿石难浸的原因，同时用实际的 关键词微细粒包体金堆浸资源利用 Research on Factors of Refractory Minerals in Beijin Ore Area of Gansu Laojinchang Gold Mine Du Shiyong2 (1. Gansu Non-ferrous Bona Mining Industry Ltd.; 2. Team 4 of Gansu Non-ferrous Metal Geological Exploration Bureau) Abstract: Based on the ore nature of Beijin ore area, and in combination with the actual production, reasons for refractory ores in Beijin gold mine are analyzed. Meanwhile, through the actual production and empirical data, it is proved that this heap leaching process do not suit this kind of ore. The research provides a good reference for rational exploration and utilization of similar ores resources in this area. Keywords: Micro-grained gold-bearing minerals, Heap leaching, Resource utilization 十几年以来，新、老金厂金矿石一直采用堆浸工0．002～0．007mm之间，裂隙金和粒间金含量达90％，包裹金含量仅为10％，这样的矿石适合于堆85％以上，1999年后，(点)，并于2000年对老金厂矿区北边10km的北3000余吨，与老金28．89％。经浅井 1 矿石性质 1．1矿石多元素分析 原矿多元素化学分析结果见表1。1．2矿石结构构造及矿物组成 矿石结构主要为自形半自形、溶蚀、残余结 1．3载金矿物特征 褐铁矿、黄铁矿是矿石中金主要的载矿物，自0．010mm粒级中褐铁矿的占有率为8．65％，而44．13％。从总体来0．074mm粒级95％做浸出试验，金的浸出率只有44．51％，仍有50％以上的金赋存在褐铁矿、黄铁矿及0．074mm占95％时，金在2。1．4自然金特征 自然金与褐铁矿关系十分密切，常以微细粒包0．005mm，常见粒度在0．002mm左右，偶0．074mm占95％时，金在各3。从表3可看出，除+0．074mm粒级外，产品粒0．037mm粒级中，金4．72g／t，其分布率为93．42％。由此可 2 北金金矿石柱浸试验 为与实际生产做比较，对北金金矿石取样做柱200kg，破10mm，混合缩分后分别装入2个试验柱中。50kg，1柱混合样品位3．49g／t，2柱3．2g／t，浸泡时间和充氧时间都为12h。试验条件和结果见表4和表5。 从表4可计算出，1柱矿样的回收率30．20％；5可计算出，2柱矿样的回收率35．10％。由此32．65％。 由柱浸试验的结果可以看出，即使使用高浓度 3 氰化堆浸工艺 堆浸法是处理低品位金矿石的一种有效方法， 3．1 实际生产中的氰化堆浸工艺和技术指标 实际生产中的原则流程如图1所示。 实际生产中的技术指标： (1)入堆粒度。因矿石含有少量泥质，氧化程50mm。 (2)氰化液浓度。根据以往实践经验氰化液浓0．02％～0．1％之间。氰化初期保持在0．08％～0．1％，中期保持在0．04％～0．08％，尾期0．02％～0．04％。 (3)氰化液pH值。pH值保持在10～12之间。 (4)氰化堆浸时间。依据堆浸工艺要求，气温10℃以上，结合当地实际情况，具体氰化8-10月。 (5)喷淋方式及强度。喷淋方式采用间歇式，即1 h喷淋1次，以便矿堆及时充氧；根据矿石的0．04～0．06 L／(t·min)。 (6)筑堆方式及堆高。筑堆采用分层法，堆高4m。 3．2实际生产中的浸出周期及浸出率 实际生产中浸出周期长达50 d左右，且浸出速3．5g／m。需要7d的时间，比以往5 d时间多出2 d时间。浸出矿石25％的金用