锰和硫元素对灰铁铸件性能的影响.pdfVIP

学兔兔 锰和硫元素对灰铁铸件性能的影响 自 飞，黄进达 (广西玉柴机器股份有限公司，广西 玉林 537005) 摘要：为提高灰铸铁材质的性能，通过正交试验分析了W(Mn)、W(s)对材料抗拉强度和硬度的 影响，发现低硫、低锰有利于改善铸件性能，并在随后的生产试验中证实了正交试验的结果。 提出在柴油机缸体、缸盖生产过程中，为了获得稳定的高强度灰铁材质，建议w(Mn)控制在 0．3％～0．5％、W(S)控制在0．04％～0．07％范围内。 关键词：灰铸铁；锰元素；硫元素；力学性能 中图分类号：TG143．2 文献标识码：A 文章编号：1673-3320(2014)02-0016-03 Effects of Manganese and Sulfur on Properties of Gray Iron Castings BAI Fei，HUANG Jinda (Guangxi Yuchai Machinery Co．，Ltd．，Yulin 537005，Guangxi，China) Abstract：To improve the properties of gray cast iron，the effects of manganese and sulfur on the tensile strength and hardness of material were analyzed by o~hogonal test．It was found that lower sulfur and lower manganese in gray cast iron was helpful to improve the casting properties，and the results of the orthogonal experiment were confirmed in the subsequent production testing．In order to obtain the stable high strength gray cast iron material in the production of cylinder block and head for diesel，an appropriate control range of manganese content(from O-3％to 0．5％)and sulfur content(from O．04％to 0．07％1 are proposed． Key words：gray cast iron；manganese；sulfur；mechanical property 灰铸铁具有非常优越的铸造性能和良好的 表1 W(Mn)和w(S)因子水平设定 综合性能，而且成本相对较低，所以很多柴油机 缸体、缸盖铸件生产厂家依然将灰铸铁作为首选 材质之一。为提高灰铸铁力学性能及降低材料成 本，本文进行了针对性的试验。 1 试验过程 1．1 试验设计 中频感应电炉熔炼，浇注 30 mm试棒。正 交试验设计为w(Mn)、w(s)两个因子在三个水平 上对抗拉强度、硬度的影响。根据以往经验及降 成本的需求，设定的w(Mn)~w(S)N子水平如表1 所示。 铁水。铁水熔化后检验成分，按照正交试验要求 1．2 试验实施 进行控制。 分别在1 、2 、3 工频炉熔化铁水，4 炉调匀 I 炉倒出两包铁水，从2 、3 炉各倒一包铁 收稿日期