缓冲基板铸件生产的关键技术.pdfVIP

学兔兔 缓冲基板铸件生产的关键技术 张太荣，欧阳代云，姚先成，徐尔灵 (广东省韶铸集团有限公司，广东 韶关 512031) 摘要：缓冲基板是建筑防震用关键部件。分析了缓冲基板的材质特性毋口成分控制，对铸件的铸 造工艺方案进行了试验论证，并确定了其热处理工艺。通过采取针对性的工艺措施，满足了铸 件材料性能要求，有效解决了产品的铸造缺陷和热处理变形等问题，并取得了较好的效益。 关键词：缓冲基板；铸钢件；工艺控制 中图分类号：TG269 文献标识码：B 文章编号：1673-3320(2011)06—0031—03 Key Technology for Damping Base Plate Casting Zhang Tairong Ouyang Daiyun，Yao Xiancheng，Xu Eding (Guangdong Shaoguan Found~and Forging Group Co．，Ltd．，Shaoguan 512031， Guangdong，China) Abstract：The damping base plate casting is a key part for quakeproof in construction．The material features and composition control of the castings were analyzed，the casting process was tested and verified．and the heat treatment process was determined。The specific process measures can meet the requirements of casting performances，and the casting defects and heat treatment deformation for productions are eliminated effectively,and me better benefits are achieved． Key words：damping base plate；steel casting；process control 日本高层建筑的柱基采用缓冲机构来保证防 提高一个等级，如表1、表2所示。 震效果。而缓冲基板是缓冲机构中最大、最关键 表1 成分要求 wB(％) 的部件，其多项质量要求远超一般铸钢件标准的 要求。自1996年起，韶铸集团有限公司的工程技 术人员克服重重困难，成功开发了缓冲基板系歹 产品，至今已累计生产了2万多吨成品，并将在 注：CE=C+ l 6+Si／24+Ni／4o+Cr／5+M0／4+v／l4 不久推出改进型产品。不断提高的材质高性能要 PCM =C+Si／30+Mn／20+Cu／2 }_Ni／40+Cr／20+】 o，l 5+ 求、高致密性要求以及四角平台平行度等问题成 V／10+5B 表2 力学性能要求 为该系列产品成功与否的关键。 1 材料的研究与控制 缓冲基板材质牌号为SN490，系从焊接结构 钢材料演变而来。其碳当量 (CE)和焊接裂纹敏 感性指数 (PCM)有严格的限制，总体成分类似