新型搅拌桨的精铸工艺.pdfVIP

学兔兔 NOV．2OO9 铸 造 VO1．58 NO．11 FOUNDRY 新型搅拌桨的精铸工艺 邵抗振，杜瑞昌，李 桐，王 拓，赵竞祥，吴现龙，李克锐，吴建基 (郑州机械研究所，河南郑州450052) 摘要：采用无余量整体精密铸道成形技术，对新型薄壁不锈钢搅拌桨精密铸造工艺进行了研究，合理设计并优化了X- 艺参数。结果表明，该工艺能够减少铸造缺陷，提高了合格率，并生产出表面质量高、尺寸精度高、附加值高的产品。 关键词：不锈钢；搅拌桨；精密铸造；工艺参数 中图分类号：TG249．5 文献标识码：B 文章编号：1001—4977(2009)1 1-1 181—02 Investment Casting Technology of New Type Stirring Paddle SHAO Kang—zhen，DU Rui—chang，LI Tong，WANG Tuo，ZHAO Jing-xiang， WU Xian—long，LI Ke-rui，WU Jian-ji (Zhengzhou Research Institute of Mechanical Engineering，Zhengzhou 450052，Henan，China) Abstract： The near net-shape integraI investment casting process of new type thin．walI frame stainless steeI stirring paddle was studied．and the technological parameters were designed and optimized rationally．The results show that casting defects were reduced and the qualified rate of castings increased．The products produced by using of the process have the merits of high surface quality，high dimensional accuracy，and high added value． Key WOrds：stainless steel；stirring paddle；investment casting；technological parameter 搅拌混合在石油、化工、医药、农药、染料、肥 成外径为6．5 mm，长度为120 mm的型芯。压蜡前将 料、食品、日用化学品与化妆品、造纸及废水处理等 型芯置于压型中，然后在M225系列压蜡机上压制蜡 行业中应用十分广泛_l】。这些工业生产离不开机械搅拌 模，将组合好的蜡模采用硅溶胶型壳方法制壳，型壳 设备，而不锈钢搅拌桨又是机械搅拌设备中的关键部 干燥后通过DN800／1000电热脱蜡釜脱蜡，然后在焙 件。搅拌桨属于复杂铸件，不仅形状复杂，还要求对 烧炉里将型壳焙烧，并在150 kg的KYPS中频感应炉 称、均衡，有的还有复杂曲面，对尺寸精度、形状精 中熔炼不锈钢并浇注成型，最后铸件经切割、清理、 度和位置精度均有较高要求[2_。目前搅拌桨毛坯主要有 焊修，并检验入库。铸件的材料选用CF一8M (316)不 砂型铸造和精密铸造两种方法生产，砂型铸造精度低， 锈钢，化学成分见表1。 加工余量大，适合大件毛坯生产；对于小型的桨通常 用精密铸造方法生产。本文中研究的新型搅拌桨是由 不同方向的l2个叶片组成的薄壁复杂铸件，叶片最厚 处2 mm，最薄处仅为0．5 mill，铸件单重只有 100 g，