感应炉熔炼与双联熔炼的灰铸铁力学性能的比较.pdfVIP

学兔兔 铸 造 Feb．2013 · 96 · FOUNDRY VOI．62 NO．2 感应炉熔炼与双联熔炼的灰铸铁力学性能的比较 童思艺 (广西玉柴机器股份有限公司，广西玉林537005) 摘要：运用数理统计的方法，统计分析了大量使用感应炉熔炼与双联熔炼灰铸铁的单铸试棒的力学性能数据，通过 比较发现：尽管铸件和材料牌号相同，化学成分、孕育剂及其加入量基本相同，原材料的规格、质量标准和产地基 本相同，但双联熔炼灰铸铁与感应炉熔炼灰铸铁相比，其单铸试棒的抗拉强度高约26．5 MPa，硬度高HBW6，冶金 质量也好。 关键词：感应炉熔炼；双联熔炼；灰铸铁；力学性能 中图分类号：TG250．2 文献标识码：B 文章编号：1001—4977(2013)02—0096—03 Comparison of Mechanical Properties of Gray Cast Iron by Induction Furnace Smelting and Duplex Melting TONG Si-yi (Guangxi Yuchai Machinery Co．，Ltd．，Yulin 537005，Guangxi，China) Abstract：Using method ofmathematical statistics，the data ofseparately cast test bar mechanica1 properties of graV iron by use of induction furnace and duplex melting were statistically analyzed．The results show that with basically the same conditions such as casting,alloy grade．the chemical composition,the inoculant addition．the specifications，quality standards and origin ofthe raw materials，the duplex melting ay iron separately cast test bars have the tensile strength 26．5 MPa and hardness HBW 6 higher than that ofinduction furnace smelting gray iron,and its metallurgical quality is better too． Key words~induction furnace smelting；duplex melting；gray cast iron；mechanical properties 当前，感应电炉应用越来越广泛，或迫于环保的 本文运用数理统计的方法，分别统计分析了大量 压力，或迫于焦炭涨价的压力，或对冲天炉的优点认 使用感应炉熔炼灰铸铁与双联熔炼灰铸铁的单铸试棒 识不足，新建的铸造车间多数采用感应电炉。但也有 的化学成分和力学性能数据，通过比较两个样本的平 些学者认为：由于缺乏冲天炉内的多相冶金反应条件， 均值，发现尽管铸件和牌号相同，化学成分、孕育方 感应电炉熔