学兔兔 建筑密封 硅氧烷交联聚氨酯密封胶 耐热老化性能的研究 李步春，毛俊轩，车国勇，熊 婷 (成都硅宝科技股份有限公司，四川 成都 610041) 摘要：通过对硅氧烷交联聚氨酯树脂老化机理的分析，选取了两种常用的受阻酚类抗氧剂：AO一1、AO一2，对比了两种抗 氧剂对硅氧烷交联聚氨酯密封胶性能的影响；并在此基础上，采用受阻胺光稳定剂与AO—l复配使用，制得了具有较优 耐热老化性能的硅氧烷交联聚氨酯密封胶。 关键词：硅氧烷交联聚氨酯密封胶；耐热老化；抗氧剂；光稳定剂 文章编号：1007—497X(2014)一18—0033—03 中图分类号：TU57 8；TU502 文献标识码：A Study on Heat Aging Resistance of Siloxane Cross-linked Polyurethane Sealant Li Buchun，Mao Junxuan，Che Guoyong，Xiong Ting (Chengdu Guibao Technology Co．，Ltd．，Chengdu，Sichuan 610041，China) Abstract：Through the aging mechanism analysis of siloxane cross-linked polyurethane resin，two common hindered phenolic antioxidants AO-1 and AO一2 were chosen to compare their influences on the performance of siloxane cross—linked polyurethane sealant．On this basis，the siloxane cross-linked polyurethane sealant possessing superior heat aging resistant property is prepared by the compounding of hindered amine light stabilizer and AO一1． Key words：siloxane cross—linked polyurethane sealant；heat aging resistance；antioxidant；light stabilizer 聚氨酯密封胶具有良好的高弹性、低温柔韧性和 硅氧烷交联聚氨酯是一种新型杂化材料，它同时 粘结强度，且耐酸碱和有机溶剂、对基材不污染、可涂 具有聚氨酯良好的力学性能、耐化学及耐磨等性能和 漆，在建筑领域应用十分广泛。但是，聚氨酯密封胶的 有机硅的耐湿热、储存稳定等性能。经硅氧烷交联改 耐热性能较差，长期使用温度不能超过80℃，短期使 性后的聚氨酯产品，其耐热老化性能在一定程度上得 用温度不能超过120 qC(热老化降解反应在80℃开 到了提高。但是，由于硅氧烷交联聚氨酯树脂的分子 始，超过 100℃时反应加速进行)ll_3l。 主链与聚氨酯分子主链类似，在受热情况下易发生分 子主链的热老化降解，导致最终产品的长期耐热老化 收稿日期：2014—06—11 性能差，在高温条件下长期放置后，力学性能会急剧 作者简介：李步春，男，成都硅宝科技股份有限公司副总经理。 联系地址：610041成都高新区新园大道l6号成都硅宝科技股 下降M。 份有限公司。