MDI与TDI聚氨酯固化剂用于双组分溶剂型聚氨酯涂料的变色对比_华成明.pdfVIP

echnical Research and Development T 技术研发 MDI与TDI聚氨酯固化剂用于双组分 溶剂型聚氨酯涂料的变色对比 □ 华成明，周俊锋，胡远奇，张 琴 （武汉仕全兴装饰涂料有限公司， 武汉 430040） 摘要:以不同2，4体含量MDI合成的聚氨酯固化剂与TDI合成的聚氨酯固化剂进行变色情况对比，结果 表明，50% 2，4体含量MDI合成的固化剂与TDI-80合成的固化剂变色相当，采用自制的80% 2，4体含量MDI 合成的聚氨酯固化剂变色程度比TDI-80合成的聚氨酯固化剂好，并对变色原因进行了理论分析和探讨。 关键词:MDI;TDI;聚氨酯固化剂;紫外加速老化;变色 中图分类号:TQ630.4+93 文献标识码:A 文章编号:1006-2556(2010)10-0035-04 Comparison of the Discoloration of MDI PU Curing Agent and TDI PU Curing Agent Used in Two-package Solvent-borne PU Coatings Hua Chengming, Zhou Junfeng, Hu Yuanqi, Zhang Qin (Wuhan Shiquanxing Decorative Paints Co., Ltd., Wuhan 430040, Hubei Province) Abstract:Through comparing the discoloration of PU curing agents from MDI with different 2,4 group content with the discoloration of PU curing agent from TDI, it is showed that the discoloration of PU curing agent from MDI with 2,4 group content of 50% is equivalent to PU curing agent from TDI-80; and the property of the curing agent from self-made MDI with 2,4 group content of 50% is better than the curing agent from TDI-80. And this paper theoretically analyzes the reason of discoloration. Keywords:MDI, TDI, PU curing agent, UV accelerated aging test, discoloration 0 前 言 聚氨酯产业的发展方向。然而，一直以来涂料工作者 二苯甲烷二异氰酸酯（MDI）与甲苯二异氰酸酯 对MDI的认知存在一定的误区，认为MDI有一些缺 （TDI）相比，具有低毒性、低蒸气压的环保优点，在双 点，其中之一是其变色比TDI严重。据资料显示，4，4 组分聚氨酯涂料应用中还因为其特殊的分子结构具 结构的MDI合成的聚氨酯，由于光老化时会形成颜 有柔韧性好[1]、而且MDI预聚物中的—NCO与—OH 色较深的双醌酰亚胺结构，变色比TDI-80合成的聚 活性高[2]导致涂膜实干快的特点，这些特点使MDI代