无铅镉陶瓷颜料生产及应用研究..docVIP

无铅无镉陶瓷颜料生产及应用研究* 李伦2 殷书建1 桑爱美1 樊震坤1 孙立香1 刘宝英1 刘德军2 （1.山东省硅酸盐研究设计院，淄博255086；2.山东硅苑新材料科技股份有限公司，淄博 255086） 摘要 本文通过对无铅无镉陶瓷颜料关键技术的研究，阐述了无铅无镉陶瓷颜料在生产和使用过程中应该注意的一些问题，指出日用陶瓷产品只有从原材料、装饰材料和生产的各个环节严格把关，才能有效地控制铅、镉溶出量，彻底从源头上杜绝铅、镉等有害元素对环境的污染问题。 关键词 无铅无镉 陶瓷颜料 铅溶出 镉溶出 标准 原料 检验 RESEARCH ON PRODUCTION AND APPLICATION OF LEAD-CADMIUM-FREE CERAMIC COLORS Lilun2 Yinshujian1Sangaimei1 Fanzhenkun1 Sunlixiang1Liubaoying1 Liudejun2 (1 Shandong Institute of Silicate Research and Design Zibo 255086, 2 Shandong Institute of Advanced Ceramics Co., Ltd. Zibo 255086) Abstract Based on a research on the key techniques of lead-cadmium-free ceramic colors, This report mainly focuses on a few problems need paying attention to during the process of production and application of the lead-cadmium-free ceramic colors. There should be a strict restriction on raw materials, decorative materials and also every process of the production. Only in this way, can we control the lead release and cadmium release effectively and prevent environmental issues caused by lead and cadmium and other toxic elements from the very beginning. Key Words Lead-cadmium-free， ceramic colors， Lead release，Cadmium release，Ceramics，Standard，Raw-materials， testing 前言 含铅、镉陶瓷颜料因其性能优良，长期以来被广泛使用；随着科技的发展和社会的进步，其危害性引起了人们的高度重视。含铅、镉颜料在生产过程中会污染环境，生产工人为第一受害者；用含铅、镉颜料装饰的食器具长时间盛放酸性食物、酸性饮料和酒的时候，铅的溶出量会成倍的增大，对食物造成污染；铅镉以各种方式进入人体后，都会对人体健康造成危害、甚致死亡。因此世界发达国家的立法越来越严格，2005年欧盟委员会发布2005/31/EC指令，对1984/500/EEC指令《关于与食品接触的瓷器制品的性能标准与合格声明》进行了修订，并且要求所有不和食品接触的陶瓷产品必须增加永久标识，类似“请勿用于食物或饮品，本产品含有铅(镉)”等，要求生产商和欧盟的进口商须出具适当的产品铅镉溶出量证明，从2007年5月20日开始，禁止不符合条件的陶瓷产品进入欧盟各国。Cd含量 PbO≤30ppm，CdO≤30ppm 物质含量EPA3050B检测方法 颜料含水率（%） 小于0.4 色差 △E1.5 PH值 7～8 彩烤温度（℃） 820～900（烤烧时间为60～90min） 釉上颜料 颗粒度 直径小于15μ的颗粒不少于95%，最大颗粒不超过25μ Pb溶出量（㎎/L）Cd溶出量（㎎/L） 参考资料 秦建芳等，谈无铅化陶瓷装饰的标准及无铅颜料的应用，山东陶瓷，2008.1 于淑艳等，对我国陶瓷产品出口困境的理性思考，山东陶瓷，2008.3 张新华等，无铅无镉陶瓷釉上颜料的应用，山东陶瓷，1998.4 殷书建等，无铅无镉陶瓷釉上颜料研究，山东陶瓷，1995.3 殷书建等，无铅无镉陶瓷釉上颜料助熔剂的进一步研究，中国陶瓷工业Boffee, M.; Letocart, G.: The i