芳纶纤维的研究进展及其应用 摘 要 芳纶全称为“聚对苯二甲酰对苯二胺”，是一种新型高科技合成纤维，具有超高强度、高模量和耐高温、耐酸耐碱、重量轻、绝缘、抗老化、生命周期长等优良性能。 芳纶纤维背景发生于20 世纪60 年代末，最初作为宇宙开发材料和重要的战略物资而鲜为人知。冷战结束后，芳纶作为高技术含量的纤维材料大量用于民用领域，才逐渐露为人所知。 从全球市场及国内供求关系方面的市场分析，产能明显不足。 随着欧美地区开展禁止使用石棉的环境保护运动，芳纶浆粕纤维得到了迅速的发展，在其他工业领域、民用领域中也得到了广泛的应用。 Abstract Aramid fiber is called poly-para-phenylene two benzoyl two of benzene amine, is a new high-tech synthetic fiber, has excellent properties of ultra high strength, high modulus and high temperature resistance, acid resistance and alkali resistance, light weight, insulation, anti-aging, long life cycle. Aramid fiber background occurred in the late nineteen sixties, initially as the universe development material and an important strategic material and little-known. After the end of the cold war, aramid fiber as fiber material with high technology content is widely used in civilian areas, gradually exposed known. From the analysis of relationship between the global market and the domestic supply and demand of the market, production capacity is obviously insufficient. Along with the development of the environmental protection movement banned the use of asbestos in Europe and the U.S., aramid pulp fiber has been rapid development, has been widely used in other industrial field, civil field. 关键词：芳纶，背景，市场分析，应用 Keywords: aramid, background, market analysis, application 1.绪论 1.1 芳纶纤维的概述 1.1.1 芳纶纤维的定义 至少有85%的酰胺链(-CONH-)直接与两苯环相连接。根据此定义，可把主要化学链和环链脂肪基的一般聚酰胺聚合物和其清楚的分开。 1.1.2 芳纶纤维的分类 芳纶主要分为两种，对位芳酰胺纤维（PPTA）和间位芳酰胺纤维（PMIA）。 1.2 芳纶纤维的特点 1、良好的机械特性 间位芳纶是一种柔性高分子，断裂强度高于普通涤纶、棉、尼龙等，伸长率较大，手感柔软，可纺性好，可生产成不同纤度、长度的短纤维和长丝，在一般纺织机械制成不同纱支织成面料、无纺布，经过后整理，满足不同领域的防护服装的要求。 2、优异的阻燃、耐热性能 间位芳纶的极限氧指数(LOI)大于28，因此当它离开火焰时不会继续燃烧。 3、稳定的化学性质 间位芳纶具有优异的耐大多数化学物质的性能，可耐大多数高浓度的无机酸，常温下耐碱性能好。 4、耐辐射性 间位芳纶的耐辐射性能十分优异。例如在1.2×10-2 w/in2紫外线和1.72×108rads的γ射线的长时间照射下，其强度仍保持不变。 5、耐久性 间位芳纶优良的耐摩擦和耐化学品性能，经过100次洗涤后，用纽士达reg;间位芳纶加工的布料撕破强力仍可以达到原强力的85%以上。 对位芳纶的耐温性能要高于间位芳纶，连续使用温度范围为-196 ℃ ～ 204 ℃，在560℃高温下不分解、不熔化。对位芳纶最显著的特性是高强度、高模量，其强度大于25克/旦，是优质钢材的5～6倍、玻纤的3倍；