《织构化AZ31B镁合金在不同温度下的成形极限(英文期刊)》.pdfVIP

Forming limit of textured AZ31B magnesium alloy sheet at different temperatures 1, 2 1, 2 1 1, 2 1, 2 HUANG Guang-sheng , ZHANG Hua , GAO Xiao-yun , SONG Bo , ZHANG Lei 1. College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China; 2. National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing 400044, China Received 25 September 2010; accepted 20 December 2010 Abstract: Repeated unidirectional bending (RUB) was carried out to improve the texture of commercial AZ31B magnesium alloy sheets. All specimens were prepared in the rolling direction. The forming limit diagrams (FLDs) of AZ31B magnesium alloy sheet were determined experimentally by conducting stretch-forming tests at room temperature, 100, 200 and 300 °C. Compared with the as-received sheet, the lowest limited strain of AZ31B magnesium alloy sheet with tilted texture in the FLD increased by 79% at room temperature and 104% at 100 °C. The texture also affected the extension of the forming limit curves (FLC) in the FLD. However, the FLCs of two kinds of sheets almost overlapped at temperature above 200 °C. It can be concluded that the reduction of (0002) texture intensity is effective to the improvement of formability not only at room temperature but also at low-and-medium temperature. The effect of texture on FLDs becomes weak with increasing temperature. Key words: magnesium alloy sheet; repeated unidirectional bending; texture; formability; forming limit diagram reduction of (0002) basal plane texture dramaticall