_日本现代低碳和超低碳钢的冶金行为和应用的研究.pdfVIP

日本现代低碳和超低碳钢的冶金行为和应用的研究 武智弘 （福岗工业大学） 摘要 这十年中IF 钢在生产和质量方面有显著的进步，其工艺已延伸到诸如高强度钢、热浸 镀锌铁素体不锈薄钢板等很宽广的钢种上。估计在1996 年，日本生产了940 万吨IF 钢，为 了维持这么大的产量，研究工作也得到促进。 本文描述的是从1994 年东京会议以来在日本目前提出的研究课题。 Research on Metallurgical Behavior and Application of Modern LC and ULC Steels in Japan Hiroshi Takechi IF steel has remarkably progressed in production and quality in this decade, and extended the technology to wider steel grades such as high strength, hot dip galvanized, and ferritic stainless sheet steels. It is estimated that 9.4 million tons of IF steel have been produced in Japan in 1996, and the researching activities have also been promoted to sustain the enormous production. This paper describes about current topics on the activities which have presented in Japan mainly since the conf. in Tokyo, 1994. 1、再结晶织构的模型化和化学成分对r 值的影响 为什么IF钢的r 值如此之高，已争论了很长时间。 Abe1）指出Mn-C偶极子 的有害作用，它阻碍再结晶时{111}取向的成长。按照他的意见，Mn-C偶极的形 成能力可以写成公式（1） Cd/Cs=6 ·Mn （1-C ）·exp （-△ε/KT ） ( 1) Mn 此处Cd、Cs和CMn分别为Mn-C偶极子，C和Mn 的克分子浓度，T是再结晶温 度（650℃），而△ε是Mn和C之间的反应能 （-0.26eV ）。假定在热轧带钢中溶解 C可以用时效指数（AI ）来说明，相当于Mn-C偶极子形成能力的参数X如公式（2 ） 所示： X=Cd/ （Cs+Cd ）·AI (2) Kojima等人2 ）在图1 中示出了退火后X-值与{222}强度之间的关系，Osawa等 3 ）研究了用碳含量表示的Mn%和r 值之间的关系，如图 2 。他们解释说，C%在 0.002%和0.007%之间时，增加Mn%使r 值降低是由于Mn-C偶极子的作用。超低 C含量，同时添加Ti或Nb就消除Mn-C偶极子，使{111}再结晶织构平稳地形成。 这些年来，对冷轧和再结晶晶粒之间的织构进行了大量的研究。Urabe等4 ）设 想基于贮存能和围绕〈110〉轴的选择生长理论一道构成定向形核理论，并对再 结晶织构的生成进行了计算机模拟。他们证明了当环绕 〈110〉轴转动22 °，同 时改变选择{110} 〈110〉滑移系统时，在图3 中观察到的织构与在图4 中计算出 来的十分一致。 Senuma等5）报道了在α- γ区带润滑热轧能有效改善冷轧和退火后的IF 钢 的r 值，如图 5 所示。润滑减少薄板表面的剪切，它对最终退火时{111}织构形 核是有害的。连续热轧工艺的发展使IF钢带润滑热轧已在工业上应用。 经验发现当采用罩式炉退火时，Cr、V和B三元素对r 是有害的。也对在连续 退火过程中元素B 的作用进行了研究，因为B是必须加入以防止冷加工脆性，Haga 等人6）指出B恶化r 值，呈线性关系，如图 6 所示