带钢热镀锌超薄镀层研究(吉瑞化工).pdfVIP

带钢热镀锌超薄镀层研究 （吉瑞化工） 李九岭， 汪晓林 （武汉市吉瑞化工科技有限公司，湖北，武汉，430074） 2 摘要：带钢热镀锌国标中规定，最薄锌层重量为80g／m （双面），而用户需要80g 2 ／m （双面）一下的锌层重量时，则只有选择价格较贵的电镀锌板，本文从外力及内力着 手，研究出了带钢热镀锌超薄镀层的生产方法，为在一定范围内热镀锌板取代电镀锌板，降 低加工成本开辟了新的途径。 关键词：带钢热镀锌 薄镀层 气刀喷吹外力 锌液流动性 ResearchonUltraThinCoatingMassforSteelStripHotDippedGalvanizing 1 2 3 YuanSi-sheng ,LiJiu-ling ,WangXiao-lin (1. Chongqing Iron Steel Plant, Chongqing 000000, China 2. Cold Strip Rolling Mill, Wisco, Wuhan 430083, China 3. Wuhan JEWEL Technology Co.,Ltd, Wuhan 430070, China) Abstract: In national standard of hot dipped GI product, the thinnest coating mass can 2 reach80g/ m (doublesides). Sowhen customerswant productswith coating mass less 2 than 80g/ m (double sides), they can only turn to choose expensive electrogalvanzing product.Thisarticlefindsoutthesolutionto produceultrathin GIproductsbyfocusing on boththe internal and external causes so as to find away of replacing electrogalvanizing products by hot dipped galvanizing products in certain range and finally reduces productioncost. Keywords: hotdippedgalvanizing,ultrathincoatingmass,sprayingpressureofairwiper, liquidityofliquidzinc 1 实现超薄镀层的意义 热镀锌薄钢板有室外和室内两大使用领域：在室外使用时遭受风吹雨打，腐蚀环境十分 恶劣，要求厚锌层；在室内使用时，例如家具及家用电器等，为了提高装饰性，常常是锌层 和非金属涂层联合使用，形成双层保护体系，这时就要求薄锌层。我国带钢连续热镀锌国 2 2 2 中规定，最薄锌层为80g／m （双面），人们常常把标准之外40g／m ～80g／m （双面） 的带钢热镀锌锌层厚度称为超薄镀层。现代化带钢连续热镀锌的发展趋势是向高速化大型化 发展，而速度越高锌层越厚，无法满足用户薄镀层的需求，被迫使用镀层较薄的电镀锌薄钢 板，而使用电镀锌板时其价格上升20%，这是长期困惑薄锌层使用领域的难题。本文研究 了带钢连续热镀锌超薄镀层的生产方法。 2 影响锌层厚度的因素 2.1 速度的影响 1 带钢离开锌锅时，速度越高带锌越多，则相应锌层就越厚，见表 1。 表1 带钢速度与锌层重量的