X80管线钢埋弧焊焊丝用盘条SGM80的开发.pdfVIP

X80管线钢埋弧焊焊丝用盘条 SGM-80的开发 陈延清 杜则裕 许良红 郭占山 (首钢技术研究院) (天津大学) 摘 要 以Q／SYGJX0102--2007 《西气东输二线管道工程用螺旋缝埋弧焊管技术条件》为依据，采用 Mn．Mo．Ti．B合金系成功研制了一种高韧性 X80管线钢埋弧焊焊丝用盘条 SGM一80，该盘条钢质洁净，硫、 磷、氧和氮等杂质元素含量低，拉拔性能 良好。SGM一80盘条加工成的埋弧焊焊丝 H80与管线钢专用烧结 焊剂 F80匹配，熔敷金属具有较高的强度和韧性，与首钢 X80管线钢匹配 良好 ，且钢管焊缝金属的力学性 能满足技术条件要求。 关键词 X80 埋弧焊焊丝 熔敷金属 焊缝金属 DevelopmentontheRodSGM -80ofSubmergedArcW elding W ireforX80PioelineSteel CHEN Yanqing · DU Zeyu XU Lianghong GUO Zhanshan (ShougangResearchInstituteofTechnology) (TianjinUniversity) Abstract Based on the technoloyg condition ofspiral submerged weld pipe for the westgas transferringeastpipelineproject，ahigh toughnesswirerod SGM一80 forX80pipelinesteel submergedweldingwireswasdevelopedbyusingMn-Mo—Ti—B alloysystem．Therodhasverywell drawingperformance，andtheimpurityelementsinitsuchasS，P，O，N isvery low．Thedeposited metalhasveryhighstrengthandhightoughness，whichisweldedbythesubmergedweldingwiresby usingSGM-80 wire rod matching with specialsintered flux．Thewire rod matched wellwith ShougangX80pipelinesteel，andthemechanicalpropertiesofthepipelineweldmeetsthedemand ofthetechnologyconditionofspiral submergedweldpipeofrthewestgastransferringeastpipeline pmject． KeyWords X80，wireofrsubmergedarcwelding，depositedmetal，weldmetal 油气管道特别是天然气管道发展的趋势是采 钢级最高的钢种，具有高强度和高韧性的特点， 用高压输送方式，使用大 口径、高级别的管材可 与其配套的焊接材料在要求高强度的同时，还要 以大幅度节约管道建设成本 1]。 目前，X80管 求具有 良好的低温冲击韧性。对于 l219mm、 线钢作为新一代高性能管线 18．4mm厚 的X80级螺旋焊管 ，采用 已有的焊 钢已进入规模化应用阶段，国外 已建成的 丝进行焊接，虽然其熔敷金属韧性可满足要求， X80管线长度约为2000km，TransCanada公司 但强度达不到等强匹配要求，因此，有必要开发 已将 X80管线钢作为新建输气管线的基本选材。 高强度、高韧性的埋弧焊焊丝。首钢与宝鸡石油 我国2008年初启动的西气东输二线工程主干线 钢管有限责任公司 (简称宝鸡钢管)于 2006年 全部采用 X80管线钢 ，用量达 355万 t。X80管 开始进行 X80管线钢埋弧焊焊