在役预应力混凝土结构耐久性检测与修复.pdfVIP

在役预应力混凝土结构耐久性检测与修复 王 玲 郭小华 洪 光 （中冶建筑研究总院有限公司，北京100088） 摘 要：在役预应力混凝土结构耐久性问题成为国内外工程界关注的课题。本文以现有普钢筋混凝土结构耐久性的 检测与修复技术为基础，结合预应力混凝土结构的特点，提出预应力混凝土结构与普通混凝土结构耐久性检测的相 同之处与不同之处。同时针对预应力混凝土结构耐久性引起的破坏，采取相应的修复措施。 关键词：在役预应力混凝土结构；耐久性；检测；修复 DURABILITY MONITORING AND REHABILITION OF EXSITING PRESTRESSED CONCRETE STRUCTURE Wang Ling Guo Xiaohua Hong Guang Abstract: The durabilty of exsiting pressed concrete structure is the question arising the attation of domestic and oversea engineering. This paper, on the base of durability of monitoring and rehabilition technology of existing reinforced concrete structure, combining with the characteristics of pre-stressed concrete structures, put forward on the similarities and differences between the pre-stressed concrete structure monitoring and concrete structure. Also for the damage of pre-stressed concrete structures due to durability, it outline several repair technology. Keywords: exsiting pressed concrete structure ；durability ；monitoring ；rehabilition 与普通混凝土结构和钢结构相比, 现代预 收缩，产生孔隙，致使粘结强度不足，也会影响 应力混凝土结构不仅结构性能优越, 而且能充 耐久性。 分地发挥高强度材料的性能, 具有较高的经济 2 ）普通钢筋锈蚀时，会在表面产生锈斑， 效益, 从而可以节约能源，在世界各国都得到了 引起混凝土保护层的剥落、层裂等外在现象，而 广泛的应用。 预应力钢丝在很多情况下，会发生无任何预兆的 与普通钢筋混凝土耐久性相比[1]，预应力混 脆性断裂，导致结构的突然破坏。预应力筋的锈 凝土结构的耐久性既有相同之处，又有不同的地 蚀较为复杂，除普通钢筋发生的电化学腐蚀外， 方，一般认为有以下两点主要的区别： 还有其特有的应力腐蚀。预应力筋的截面较小， 1）预应力混凝土结构施工比较复杂，技术 自开始张拉一直就处于高应力状态下，对应力腐 含量较高，每一环节的疏漏都有可能使其耐久性 蚀极为敏感，而且自腐蚀开始至失效过程很短， 能下降。整体施工过程要经历多道工序，芯管的 表现为明显的脆性破坏形态。在有应力腐蚀的情 埋置、预应力筋的张拉及锚固、管道的灌浆、锚 况下，当钢筋的应力远低于极限抗拉强度，钢筋 具的防腐处理等，每一道环节的质量缺陷都有可 就会出现裂纹或破坏。所以，在预应力混凝土的 能影响结构的耐久性。在上述