电炉流程生产含B弹簧钢的工艺实践.pdfVIP

电炉流程生产含 B 弹簧钢的工艺实践 肖洪文 黄省余 陈 明 （方大特钢科技股份有限公司，南昌 330012 ） 1 摘 要 含 B 弹簧钢具有性能适应性强、成本低、冶炼控制难度大的特点。本文分析了方大特钢电炉生产含 B 弹 簧钢的原料、初炼、精炼、连铸、缓冷等工艺控制措施及作用，通过优化炉料结构与终点碳控制，复合脱氧保硼工 艺操作和连铸工艺技术的综合运用控制，实现了含 B 弹簧钢的连续化大批量生产。 关键词 电炉流程 含 B 弹簧钢 工艺控制措施 Technological Practice of B-bearing Spring Steel Produced by EAF-LF-CC Process Xiao Hongwen Huang Xingyu Chen Ming (Fangda Science and Technology of Special Steel Co.,Ltd.，Nanchang ，330012) Abstract B-bearing spring steel have the characteristics of adaptable capability，low cost and smelting difficult to control. This article analyzed the process controlling measures of material, smelting, refining, continuous casting and slow cooling in Electric-Furnace plant of principal company. Continuous mass production of B-bearing spring steel has been achieved through the optimizing control furnace charge structure and terminal carbon, complex deoxidation technique for saving boron, application and control of continuous casting technique. Key words EAF-LF-CC process ，B-bearing spring steel ，controlling measures of process 1 引言 合金弹簧钢中加硼，一般是为了提高钢的淬透性，因为硼对淬透性贡献最大，0.001%～0.003%硼的作 用分别相当于含 0.6%Mn、0.7%Cr、0.15%Mo、1.5%Ni，因此可以节约大量合金元素。而且钢中碳含量减少， 硼的淬透性效应越发突出[1,2] 。研究还发现：硼能提高钢的抗弹减性，因为当硼原子以间隙形式固溶于奥氏 体、铁素体中时，特别容易聚集在位错线附近，阻碍位错运动，抑制变形过程[3] ；硼可以提高钢的塑性，认 为硼优先渗透进入晶界，可以控制磷的晶界偏析，从而防止晶界脆化[4] 。所以，国内外弹簧钢标准中及高性 能弹簧钢新品研发、应用上，均出现了不少含 B 的合金弹簧钢。如：我国标准中就有 55SiMnVB、60CrMnBA、 28MnSiB，分属 Si-Mn 系弹簧钢和 Cr-Mn 系弹簧钢，它们的碳含量差别很大；而我国研发的变截面板簧产 品38SiMnVB，属中碳 Si-Mn 系弹簧钢；我公司与国内某著名汽车公司共同开发生产的低成本替代型某钢号 弹扁钢，则属中高碳 Cr-Mn 系弹簧钢。由此可见，含 B 弹簧钢涉及的合金钢种范围较大，其生产工艺控制 远比一般弹簧钢的要求苛刻、复杂。下面就我公司电炉厂生产含 B 弹簧钢的工艺控制及其措施效果做一简 要介绍。 肖洪文（1961-），男，高工，现主要从事炼钢工艺技术管理及新品研发，E-mail ：xiaohongwen2007@ 8-696 第八届（2011 ）中国钢铁年会论文集 2 生产工艺流程及主要设备