电渣重熔含钛不锈钢工艺研究.pdfVIP

电渣重熔含钛不锈钢工艺研究 李建军 史永林 ( 山西太钢不锈钢股份有限公司，太原 030003 ) 1 摘 要 采用非气氛保护电渣炉重熔含钛不锈钢 321 后, 低倍检验结果和夹杂物级别较好，符合产品标准要求,但是 Ti 烧损较大，钛含量由 0.28% 降为 0.027% ，烧损率为 90%，通过分析烧损机理，提出了采用提纯渣重熔、全程 氩气保护并适当降低熔化功率等新工艺。试验表明：采用新工艺后，低倍检验结果和夹杂物级别变化不大，但 Ti 烧损大大降低，钛含量由 0.28% 降为0. 27%，烧损0.01% ，烧损率仅为3.6%，取得了满意的效果。 关键词 含钛不锈钢 321 电渣重熔 提纯渣 氩气保护 Process Study on Electro-slag Remelting (ESR) of Titanium-bearing Stainless Steel Li Jianjun Shi Yonglin (Shanxi Taigang Stainless Steel Co., Ltd., Taiyuan ,030003) Abstract In the process of Electro-slag remelting (ESR) of titanium-bearing stainless steel 321 at non-protective atmosphere, Ti burning is significant and the Ti content reduce from 0.28% to 0.027%, the burning loss rate of Ti is 90%. By analyzing the burning mechanism, new technology are proposed such as purification melting, protection of argon through the whole process and reduction of the melting power. After the introduction of new technology, the results showed that Ti burning reduced greatly to 0.01%, burning loss rate is 3.6%. Key words Titanium-bearing stainless steel 321 ，ESR, purification slag，argon protection 太钢已成为全球最大的不锈钢生产基地，过去大都生产板材，电渣不锈钢数量较少，随着不锈钢在航天航 空、军工、能源、船舶、电子、石化、重型机械和交通等许多国民经济的重要领域的应用，大型不锈钢型材也 越来越得到广泛的应用，由于电渣重熔具有设备简单，易于操作，成本较低的优点，除去气不及真空电弧重熔 外，在结晶组织、钢锭表面光洁度、脱硫及去除夹杂物能力方面均优于真空电弧重熔。因此，许多航天航空、 军工、能源材料转向由电渣重熔生产。太钢为满足顾客需求，顺应新趋势，决定开发电渣重熔不锈钢 321 工艺。 1 试验设备 本次试验电渣炉设备主要技术参数如下： （1）变压器。 型号：HEDSPZ—3500/10； 额定容量：2205kW ； 一次电压：10000V； 二次电压：50～105V； 李建军（1971—），男，硕士，现在山西太钢不锈钢股份有限公司技术中心工作, 电话：0351-3011556, lijj01@ 8-80 第八届（2011 ）中国钢铁年会论文集 最大工作电流：18000A （低压端）； 级数：27 级； 级差：1～3V； 变压器采用带载电动调节。 （