铁矿球团适宜MgOSiO2比值的试验研究.pdfVIP

铁矿球团适宜 MgO/SiO2 比值的试验研究 黄永君 韩晓东 （鞍钢股份公司炼铁总厂，鞍山 114021 ） 1 摘 要 在实验室条件下对不同 MgO/SiO2 比值（0.044、0.38、0.54 ）的酸性球团进行试验研究。试验结果表明， 随着MgO 含量的增加，球团矿低温还原粉化率指标有所改善，还原膨胀指数明显降低，球团矿的软融开始温度提 高、软化区间变窄。即当球团矿 MgO/ SiO2 为 0.45～0.55 时，其高温冶金性能改善。 关键词 球团矿 MgO/SiO2 值 冶金性能 An Experimental Study on Reasonable Value of MgO/SiO2 Pellets Huang Yongjun Han Xiaodong (Iron-making Platnt of Ansteel, Anshan, 114021) Abstract an experimental study on acid pellets with different MgO/SiO2 (0.044 、0.38、0.54) in lab-scale has been carried out, and it was shown that, the low temperature reduction degradation rate has been improved with an increasing MgO, the expanding rate was lowered definitely, and the softening temperature and interval became higher and smaller separately. While the MgO/ SiO2 is from 0.45 to 0.55, the high-temperature metallurgical properties were improved. Key words pellets MgO/ SiO2 metallurgical properties 1 引言 向高炉炉料中合理添加 MgO ，从而改善铁矿石的高温冶金性能已有许多报道并形成共识。国外已有 100%球团矿冶炼的记录，国内的球团矿技术与国外先进企业有较明显的差距。近年来，随着球团产量的不 断增加，球团占高炉炉料比例逐年提高，改善球团矿的高温冶金性能、增加球团矿使用比例、改善冶炼效果 越来越受到重视。 带式机球团以前设计生产酸性球团，当时的实验室研究表明，当球团的 MgO/SiO2 为 0.45～0.55 时，球 团可获得较好高温冶金性能，这是在铁精矿 SiO2 在 8%左右时的结论。由于目前带式机球团的原料条件在提 铁降硅后已发生很大改变，适宜的 MgO/SiO2 值以及对改善球团高温冶金性能的作用和效果是否发生变化有 待研究。为此，针对现行的低硅铁矿，在实验室条件下对 MgO/SiO2 比值（0.044、0.38、0.54 ）的酸性球团 进行了试验研究，造出的生球团于现场球团带式机上进行了投笼试验，试验是在带式机焙烧温度 1250℃下 进行的。 黄永君（1962—），男，工程硕士，高级工程师.鞍钢炼铁总厂球团作业区作业长 铁矿球团适宜MgO/SiO2 比值的试验研究 8-147 2 试验方法 2.1 低温还原粉化率 采用国标 GB/T13242—91 试验装置及试验方法，试样粒度 10～12.5mm，重量 500g，还原温度 500℃， 还原气体流量 15NL/min，还原气体成分为 20 ％CO、20%CO 、60%N ，还原时间 60min，还原后的样品放 2 2 在转鼓(Φ1