高速钢刀具热处理腐蚀原因和预防措施

任国进，陈顺民，祝新发，许辉(上海工具厂有限公司，上海200093)

摘要：高速钢刀具在盐浴热处理过程中，往往会由于盐中含有杂质、潮湿空气、热处理操作等原因而发生腐蚀。严格按标准控制原盐的纯净度，定时对淬火加热盐浴进行脱氧和捞渣，取消酸洗或控制酸洗时间，对淬火后的刀具严格清洗和及时回火，缩短热处理生产周期等，能有效防止高速钢刀具在热处理过程中发生腐蚀。

关键词：高速钢；腐蚀；盐浴

中图分类号：TG162.2文献标识码：B文章编号：1008-1690(2014)02-0082-04

CorrosionandPrecautionsforHighSpeedSteelCutter

DuringHeatTreatment

RENGuojin,CHENShunmin,ZHUXinfa,XUHui

(ShanghaiToolWorksCo.,Ltd.,Shanghai200093,China)

Abstract:Thecorrosionofhighspeedsteelcuttersoccursfrequentlyduringsaltbathheattreatmentowingtothe

inclusionsinsalt,moistair,heattreatmentoperationandothercauses.Topreventthehighspeedsteelcuttersfrom

corrosionduringheattreatment,thefollowingprecautionsareadopted:strictcontrolofrawsaltpurityaccordingto

therelatedstandard,regulardeoxidizationfollowedbyslagremovalofsaltbathforheatingforhardening,

eliminationofpicklingsequenceordecreaseinpicklingduration,comparativelystrictcleaningandprompt

temperingofcuttersafterhardening,decreaseinheattreatmentcycle,etc.Keywords:HSS;corrosion;saltbath

高速钢刀具在盐浴热处理过程中，由于盐浴中的杂质、环境(潮湿空气等)及操作等因素的影响，往往会产生腐蚀，即表面出现针孔状或斑块状凹坑，通常称之为麻点。腐蚀严重时会降低刀具的精度和使用价值，甚至成为废品，给企业带来经济损失。因此，在热处理过程中应特别注意防止刀具腐蚀。

1产生腐蚀的原因

从目前的热处理设备、工艺条件和操作环境进行分析，高速钢刀具产生腐蚀麻点的原因大致如下。

1.1加热介质

国内不少企业高速钢刀具仍采用盐浴炉热处理，加热介质都是氯化钡。氯化钡盐由于纯度不同，往往含有硫酸盐、碳酸盐、硫化物、氧化物等杂质，部分杂质在熔融状态下与钢铁反应使刀具产生腐蚀。

反应式3:

Fe(工件)+Na?SO?→FeO(腐蚀产物)+Na?SO?

2Fe+2Na?SO?→2FeS(腐蚀产物)+30?个+2Na?O

Fe+CO?→FeO(腐蚀产物)+CO个

此外氯化钡盐常含有结晶水(BaCl?·2H?O),

当炉内添加新盐时，会促使盐浴中氧化物增加，导致工件产生腐蚀，其主要反应：

Fe(工件)+2HCl→FeCl?(腐蚀产物)+H?个

收稿日期：2012-10-19

作者简介：任国进(1970-),男，江苏海安人，硕士研究生，主要从事材料工程技术研究工作。联系电话：021·82·《热处理》2014年第29卷第2期

1.2盐浴中氧化物

盐浴在使用过程中，将有空气中的氧溶入，带锈的工件进入盐浴加热时氧化层的分解，以及加热时电极自身的熔化，均使盐浴中的氧化物含量逐渐增加，如不及时脱