大桥节点模型铸钢件的热处理和焊接工艺

蔡娟

(上海宏钢电站设备铸锻有限公司，上海200240)

摘要：基于大桥节点模型铸钢件的结构特点和技术要求，进行了试块的热处理工艺试验，通过调整材料成分改善其力学性能；为控制薄壁铸钢件焊接变形和应力，确定了节点模型的补焊工艺。按制定的工艺对节点模型进行热处理和补焊，经无损检测所有铸件均合格，避免了薄壁铸钢件在热处理和焊接时出现的缺陷。

关键词：薄壁铸钢件；热处理；焊接

中图分类号：TG161文献标识码：B文章编号：1673-3320(2015)01-0044-03

HeatTreatmentandWeldingProcessofJointModelSteelCastingforBridge

CAlJuan

(ShanghaiHonggangPowerStationEquipmentForgingCastingCo.,Ltd.,Shanghai200240,China)

Abstract:Basedonthestructurefeaturesandtechnicalrequirementsofjointmodelsteelcastingforbridge,theheattreatmentprocessofsamplepiecesweretested.Theirmechanicalpropertieswereimprovedbyadjustingthematerialcomposition.Tocontroltheweldingdeformationandstressofthin-walledsteelcastings,therepairweldingprocessofjointmodelwasdetermined.Theheattreatmentandrepairweldingofjointmodelwascarriedonspecifiedprocess,allcastingswerequalifiedbynondestructivetesting.Thedefectsofthin-walledsteelcastingsduringheattreatmentandweldingareavoided.

Keywords:thin-walledsteelcasting;heattreatment;welding

收稿日期：2014-06-25

作者简介：蔡娟(1980—),女，工程师，主要从事汽轮机铸钢件焊接与热处理的现场技术管理及工艺编制

图1试验铸件

4结论

1)中温磷化液的配置参数直接影响其防锈能力，需要根据各企业铸件的情况确定。

2)中温磷化工艺的防锈能力优于常温磷化工艺。

3)仅采用中温或高温磷化，而无后处理的工艺达不到铸件防锈要求。

4)含油成分的防锈液性能优于无油成分的防锈剂。

参考文献：

[1]蒋文军.锌钙系防锈磷化工艺[J].合肥学院学报：自然科学版，2006,16(增刊):30-32.

[2]唐春华，唐彬.功能性磷化工艺：第二部分模具磷化与耐磨、防锈复合磷化[J].电镀与涂饰，2006,25(11):31-33.

2015年第1期45

学免兔www.xuetut

大桥节点模型铸铟件的

随着我国建筑业的快速发展，建筑造型越来越复杂，结构形式越来越新颖，钢结构在建筑中的应用也越来越频繁。其中高强度钢结构和超高层钢结构的发展，使钢结构的构件和节点出现了许多新型式。针对杭州湾跨海大桥上的节点模型薄壁铸钢件，公司与同济大学合作，对节点模型的结构设计和热加工工艺进行了联合研制。

1节点模型结构及性能要求

大桥节点模型的结构如图1所示。

图1节点模型结构

节点模型铸钢件的材质按德国DIN17182-1992的要求控制，材料牌号GS-20Mn5V,其主要化学成分和力学性能分别见表1和表2。

表1节点模型材料的主要化学成分wg/%

C

SiMnP

0.17～0.23

≤0.601.00～1.50≤0.025

S

CrMoNi

≤0.020

≤0.30≤0.15≤0.40

衣2

节点模型材料的力学性能指标

Rpo.2/MPa

Rm/MPaA/%