c1160-97中文版-抗化学腐蚀碳砖的标准规范.doc

C 1160 PAGE 768 Designation: C 1160–97编号：C 1160–97 PAGE 766 Standard Specification for Chemical-Resistant Carbon Brick1抗化学腐蚀碳砖的标准规范 This specification is under the jurisdiction of ASTM Committee C-3 on Chemical-Resistant Nonmetallic Materials and is the direct responsibility of Subcommittee C03.04 on Chemical Resistant Construction Units.本试验方法受ASTM委员会C-3耐化学腐蚀的非金属材料委员会管辖，并且由C03.04耐化学腐蚀施工单位分委会直接负责。Current edition approved March 10, 1997. Published March 1998. Originally published as C 1160-90. Last previous edition C 1160-90.现行版本于1997年3月10日批准，并于1998年3月出版。最初版本编号为C1160-90，上一版本编号为C1160-90。 This standard is issued under the fixed designation C 1160; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.本标准以固定编号C1160刊发；紧随编号后的数字表示最初采用的年份，或者是修订版的最后修订年份。圆括号中的数字表示必威体育精装版重新批准的年份。上标(ε)表示自上一修订版或重新批准后的编辑性修改。 1. Scope适用范围 1.1 This specification covers machine made solid uncored carbon brick produced from either metallurgical or petroleum calcined coke, baked to a minimum 1850°F (1010°C), and suitable for use in masonry construction which will be exposed to various chemicals. These units are designed primarily for industries using hydrofluoric acid, fluoride salts and high concentrations of alkalies such as sodium and potassium hydroxide. Carbon brick are normally used with carbon rilled chemical-resistant mortars.本规范包含由冶金或石油煅烧焦制造的烧制至最低温度1850华氏度（1010摄氏度）并适用于暴露在各种化学物质下的砌筑结构的机制坚固无核碳砖。这些单元主要被设计用于使用氢氟酸、氟化盐和氢氧化钠、氢氧化钾等高浓度碱的工业。碳砖通常在碳装满抗化学腐蚀灰浆时使用。 1.2 This standard does not purport to address the safety concerns associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.本标准并非旨在解决所有与标准使用相关的安全问题