萘二异氰酸酯合成现状TheDevelopmentoftheSynthesisof.pdf

化学通报 2002 年 第65 卷 w83 1,5-萘二异氰酸酯合成现状 李 芳 丛津生 薛 伟 赵 博 河北工业大学化工学院绿色化工研究所 天津 300130 摘 要 讨论了非光气法合成 1,5-萘二异氰酸酯的研究现状及存在的问题 并介绍了由 1,5-萘 二异氰酸酯合成的弹性体的优异性能及良好应用前景 关键词 1,5-萘二异氰酸酯 弹性体 非光气法 1,5-萘二氨基甲酸酯 催化剂 The Development of the Synthesis of 1,5-Naphthalene Diisocyanate Li Fang, Cong Jinsheng, Xue Wei, Zhao Bo (Institute of Green Chemical Technology, School of Chemical Engineering, Hebei University of Technology Tianjin 300130) Abstract This paper described the excellent properties of elastomers synthesized from 1,5- naphthalene diisocyanate and the prospects of its applications. The focus is laid on the discussion of the development of the non-phosgene methods by which 1,5-naphthalene diisocyanate was synthesized and the problems existed. Key words 1,5-Naphthalene diisocyanate, Elastomer, Non-phosgene method, 1,5-Naphthalene dicarbamate, Catalyst 异氰酸酯是制备聚氨酯的基础原料 由多异氰酸酯合成的聚氨酯(PU)具有较高的强度 耐 变形稳定性 高耐磨强度 高抗撕裂强度和高弹性等优异性能 广泛用于塑料 橡胶 纤维 涂料 粘合剂等领域 当今产量最大且应用最多的异氰酸酯应属甲苯二异氰酸酯(简称 TDI)和 二苯基甲烷二异氰酸酯(简称 MDI) 但由于它们的熔点偏低 因而在某些场合的应用受到限制 与MDI(熔点37ºC) TDI(熔点21ºC)相比 1,5-萘二异氰酸酯(NDI 熔点127ºC)具有较高的熔点 由它合成的PU 具有硬度高 回弹性好 耐热性好 动态性能优异 耐磨性好等优点, 可用于普 通聚氨酯不能满足要求或过早损坏的工作场合 如高温和多油脂等环境[1,2] 因此多用来作为合 成高级聚氨酯的原料 由NDI 制成的弹性体有三种类型 即浇注型PU 模压型PU 和泡沫型PU 这三种PU 与 普通PU 相比 都有其各自的优点 列举如下 (1)浇注型PU 这种PU 不仅具有聚醚型PU 的弹性 而且具有聚酯型PU 的刚性 它的最 大特点是具有优异的动态特性和耐磨性 由动态力学分析表明 在动态载荷下 浇注型 PU 的 阻尼小 回弹性高 内生热少 主要应用在高动态载荷和耐热场合 通常用来制作轮胎 密封 件 5 皮带 磨矿盘等 如在纺织工业中 锭子的转速为(6 8) 10 r/min 因而摩擦温度较高 李 芳 女 26 岁 助教 从事绿色化工的教学与研究 国家自然基金和河北省自然科学基金(298034)资助 2001-11-20 收稿 2002-05