大直径钢筋混凝土握裹力对比试验和研究.docVIP

大直径钢筋混凝土握裹力对比试验和研究 　　摘 要：通过对未锈蚀、除锈、锈蚀钢筋的混凝土握裹力对比试验研究，提出了大直径钢筋混凝土握裹力对比试验方法。从滑动变形关系曲线以及握裹强度分析了不同锈蚀程度的带肋钢筋对混凝土握裹力的影响机理，并对其是否存在影响混凝土工程的隐患提供了客观证据,有针对性地填补了国内大直径钢筋混凝土握裹力对比试验技术的空白,解决了目前锈蚀钢筋对工程质量影响因素难以界定并排除的难题。 　　关键词：钢筋、混凝土、握裹力、试验方法 　　Abstract: Based on the no rust, rust, corrosion of reinforced concrete bond strength comparison test research, put forward large diameter reinforced concrete bond strength test method. From the sliding deformation curve and bond strength of different corrosion degrees of ribbed steel bar on the grip of concrete is discussed, and the effect of concrete project the existence of hidden provides objective evidence, to fill the domestic large diameter reinforced concrete bond strength test technology gaps, solved the corroded reinforced on the engineering quality influence factors are difficult to define and to exclude the problem. 　　Key words: steel, concrete, bond strength, test method 　　中图分类号： TU377 文献标识码：A 文章编号：2095-2104（2012） 　　 　　 前言随着日本福岛核泄露事故的影响，国家发展核电的政策从过去“积极发展核电”调整为“安全高效发展核电”，中国的核电发展规模和速度出现了低潮。目前很多核电站处于停工待建状况。然而绑扎后的钢筋随着时间延长必然产生不同程度的锈蚀。但对钢筋不同锈蚀程度及除锈后对钢筋混凝土质量有何影响，采用何种检测技术以及如何减少施工单位在核电站建造期间钢筋锈蚀防护与钢筋除锈带来负担是大家所关注的问题。目前国内外虽然对钢筋锈蚀相关性能做了大量研究与报道，但缺乏针对性、系统性，尤其是缺乏针对质保要求高的核工程如何从预防、验收、处置的质量控制研究。石岛湾核电检测中心通过对高温气冷堆核电站示范工程核岛底板钢筋一系列的研究试验，开创了大直径钢筋混凝土握裹力对比试验技术的先例，并成功地应用到实际工程中，效果非常理想。它可对停工待建工程的锈蚀钢筋是否对工程质量隐患提供客观证据,并可为后继工程启动的锈蚀钢筋做出正确的可靠的处理措施。另外可减少不必要的人力物力进行除锈,降低施工成本,因此极有参考价值。 　　1.问题的提出 　　高温气冷堆核电站示范工程核岛底板钢筋混凝土浇注量约12000msup3;，设计等级C30。已绑扎钢筋约2400t，于2009年8月底绑扎完成。由于多种原因FCD未能如期实施。虽然施工单位从开始就采取了防锈保护措施，然而仍有部分钢筋表面产生不同程度的锈蚀，并伴有麻点。为充分验证锈蚀钢筋对核岛底板混凝土的影响，保证工程质量，满足大体积混凝土施工的先决条件,业主曾多次聘请了行业内专家，根据现场钢筋锈蚀状况详细研讨和分析，可能对底板钢筋质量的影响程度。石岛湾核电检测中心受业主的委托参照水工混凝土握裹力试验方法和原理，经过验证编制了用与核岛底板钢筋和同厂家同规格型号未锈蚀钢筋(基准钢筋)、除锈钢筋（按除锈工艺用钢丝刷锈)、锈蚀钢筋在相同标号混凝土条件下做握裹力对比试验的方案。此方案得到了国家核安全局组织的现场钢筋验证咨询会专家、业主和监理的认可。 　　2.大直径钢筋握裹力试验方法 　　2.1试验方法（仪器）可行性分析 　　核电工程由于质保等级要求高,底板混凝土钢筋较民用工程不但密集而且直径大,因此探索研究大直径钢筋握裹力试验方法是编制并实施试验方案的先决条件。通过验证《水工混凝土试验规程》握裹力试验方法仅适用于小直径钢筋的握裹力试验，对于大直径钢筋的握裹力试验存在以下缺陷： 　　（1）直径≥32的