第十五届全国炼钢学术会议文集 连铸气雾冷却改造及冷却制度的研发 王强 于泳 张连君 李志园 天津钢管集团股份有限公司炼钢厂 天津 300301 摘要：通过对比连铸水冷和气雾冷却的优缺点，提出了炼钢厂气雾冷却改造的必要性，介绍了改造过程中二 冷水环和水嘴的布局设计以及喷嘴和基座的设计原理，又通过分析钢的高温力学性能、铸坯表面回温以及冷 却速度的快慢确定了气雾冷却制度，经过多次现场实际测量、修正，最终确定了Ф210mm~Ф400mm规格的水 表，通过本次改造基本解决了由于冷却不均造成的“黑斑现象”，酸洗低倍表面的“星状裂纹”缺陷也有所 减轻。 关键词： 连铸 气雾冷却 高温力学性能 Abstract: From comparison of the merits and demerits between continuous casting spraying cooling and aerosol cooling, the necessity of reconstruct of aerosol cooling in steel-making mill was proposed. The distribution design of the second cooling spraying rings and nozzles, as well as the design principle of nozzles and pedestal were introduced. Moreover, the aerosol cooling rules was determined by analyzing the dynam property of steel in high temperature, the returning temperature of the billet surface and the cooling rates. Finally, the cooling rules of Ф210mm~Ф400mm specification was confirmed by actual measurement and modification at locale time after time. After then, the black macula phenomenon that caused by asymmetric cooling was basically resolved and the defect of asteroidal cracks appeared on billet surface eroded with acid also reduced. Key words : continuous casting aerosol cooling dynam performance in high temperature 1 前言 天津钢管集团股份有限公司为了扩大产品规格范围，实现更大的发展，于 2007 年建成并投产了 PQF460 轧管机组。这就需要炼钢厂在 10.5m 弧形半径的连铸机上批量生产优质的 Ф350mm、Ф400mm圆坯。 但是，随着开发工作的不断深入，我们发现有两个因素严重影响着炼钢厂的生产节奏和铸坯的质量，首先 大规格铸坯批量生产后，目前水冷系统无法满足 Ф210mm~ Ф400mm 规格的跨度，导致铸坯的内外弧冷却不 均匀，局部铸坯在二次冷却过程中因冷却过强而存在“过冷黑斑”现象 （图 1-1）；其次是 Ф350mm、Ф400mm 圆坯拉速较慢，喷水冷却系统导致了铸坯出二冷室后在矫直时温度较低，在铸坯酸浸低倍侧面发现了“星 状裂纹”缺陷（图 1-2），给后道的轧制工序留下了较大的质量隐患。因此，通过设备改造和开发合适的冷 却方式和冷却制度成为了大规格铸坯开发项目的重点和难点。