锑和混合稀土对AZ31镁合金高温变形行为的影响.pdfVIP

锑和混合稀土对AZ31 镁合金高温变形行为的影响 马庆波，刘胜新，李庆奎，刘俊，李双喜，关绍康，陈永 （郑州大学材料科学与工程学院，河南 郑州 450002 ） 摘要:借助Gleeble-1500D 型热模拟试验机，研究了锑和混合稀土对AZ31 镁合金在不同温度下 (260～420 ℃) 的热压缩流变应力和动态再结晶的影响。结果表明：AZ31镁合金的变形抗力随变形 温度的升高逐渐减小；分别加入1%RE和1%Sb后，其变形抗力显著增大，同时有效促进了热变形 过程中的动态再结晶。 关键词: 锑；混合稀土；AZ31 ；流变应力，动态再结晶 中图分类号： Effect of Antimony and Rare earth on Hot Deformation Behavior of AZ31 Magnesium Alloy Qing-bo MA, Sheng-xin LIU, Qing-kui LI, Jun LIU, Shuang-xi LI, Shao-kang GUAN and Yong CHEN (School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450002, China) Abstract: The effect of antimony and rare earth on the flow stress and dynamic recrystallization of AZ31 magnesium alloy at different temperature (260-420℃) was investigated by hot compression testing on a Gleeble-1500D thermal simulator. The results indicated that the resistance of deformation was decreased by the elevation of deformation temperature; at the same temperature, the additions of 1%RE and 1%Sb to the AZ31 magnesium could improve the resistance obviously and accelerate the dynamical recrystalization effectively. Key words: Antimony; rare earth; AZ31; flow stress; dynamic recrystallization 1 引言 镁及镁合金是迄今在工程应用中最轻的金属结构材料，具有高的比强度、比刚度，尺寸稳定 性高，阻尼减震性能好，机械加工方便，尤其易于回收利用，具有环保特性，被誉为“21世纪绿色 工程金属结构材料” ，在列车、汽车、电子、电器、通讯、航空、航天等领域具有广阔的应用前景。 [1] 目前，工业发达国家已大力着手高性能变形镁合金加工材的研究与开发 。由于镁和多数镁合金 为密排六方结构，滑移系较少，因此，其塑性加工性能较差，制约了高性能镁合金加工材的开发 与应用。 前期实验表明在AZ31镁合金中加入一定量的锑和混合稀土可以有效改善其铸态组织和力学 性能[2-3] 。在此基础上，本文通过高温热压缩变形的模拟实验，研究锑和混合稀土对AZ31镁合金 在不同温度下应力应变关系和动态再结晶的影响。 2 实验材料与实验方法 81 试验所用的AZ31镁合金由纯镁、纯铝、纯锌和Al-10%Mn 中间合金熔炼而成，再添加微量Sb 和富Ce混合稀土(RE)，其具体化学成分见表1。 表1 试验用合金的化学成分w(%) Tab.1 Chemical Composit