聚乙烯晶体.pdfVIP

聚乙烯晶体 报告人：郭瑞 2010001075 A record has been broken — the smallest-ever polymer crystals have been prepared. Their surprising shape provides crucial evidence that might help explain how polymers crystallize. NATURE|Vol 448|30 August 2007 Technology Weber et al.now report the preparation of polyethylene nanocrystals, using a nickelcatalysed process that allows the polymer to be made in water. The combination of cryo-TEM and small-angle X- ray scattering(SAXS) demonstrates that the particles consist of a single crystalline lamella sandwiched between two thin amorphous polymer layers (“nanohamburgers”). 低温透射电镜获得的稀的水溶液中颗粒的显微照片 片晶平行 于电子束 片晶垂直 于电子束 分析67个颗粒后得到：单个聚乙烯片晶直径 25.4nm和厚度6.3nm I q q SAXS 散射强度 ( ) 与散射矢量 的关系 q 4π λ sin θ 2 ( ) ( ) λ 放射波长 θ散射角 N个颗粒在单位体积V 中的散射强度 N 2 I q I q S q φ Δρ V P q S q ( ) 0 ( ) ( ) ( ) p ( ) ( ) V 实线——SAXS数据 虚线 PRISM积分方程 蔗糖体积分数 0, 6.2, 10.3, 18.0, 25.4, 37.8 vol % 纳米颗粒体积分数 1.73, 1.56, 1.44, 1.23, 1.02, 0.68 vol % 纳米分子之间的相互作用 实验体积为1.042和聚乙烯的化学成分为基础来计算得到 溶质的平均散射密度为330每立方纳米。所得的值被用来 计算图2a 中每个强度的对比差。除了最小角度的区域，测 得的SAXS强度仅仅与密度分配当量有关。 1 夹层的散射强度为： I q d αF 2 q ,α