高层住宅低温辐射供暖地面开裂分析与防治技术研究.docVIP

高层住宅低温辐射供暖地面开裂分析与防治技术研究 何朋祥 （1青岛新华友建工集团股份有限公司 青岛 266101） [摘 要 [关键词 Study on Crack Production and Prevention of Low Temperature Radiant Heating Floor in Residence Tower Building He Pengxiang (1 Qingdao Xinhuayou Construction Group Co., Ltd. Qingdao 266101) Abstract: In order to avoid crack production of low temperature radiant heating floor, based on the actual project construction, crack production areas and crack styles are researched in the residence tower building. Meanwhile the reason and factor of crack production is analysized. Based on the analysis of crack production, the reasonable methodology for crack prevention is provided from concrete mix proportion designing, construction methodology, construction stations and concrete curing etc. The technical support is provided for the application and promotion of low temperature radiant heating system. Key words: low temperature radiant heating floor, crack, prevention methodology 1前言 现代低温辐射供暖技术，伴随着新型管材的发明（如瑞士生产的PB管材、瑞典Wirborubs公司研制的PE-X管材等）而不断发展起来。到二十世纪末期，各国低温辐射供暖技术采用率得到了显著的提升，德国达到41%、瑞士为48%、法国为20%、日本为85%、韩国为95%[1]。由于该项供暖技术主要依靠辐射热进行热量传输，克服了传统对流供热方式形成的空气干燥的缺陷，且水温控制在50℃左右即可满足供热要求，显著低于传统供热温度，在节能环保方面具有突出的技术优势，正得到越来越多的认可。 目前，国内低温辐射供暖施工技术主要是在浇筑的现浇楼板铺设复合保温板材厚度20mm的聚苯已烯泡沫板容重18~20kg/m3，然后铺设PE-Xa管材并用U型固定卡钉固定，交联管铺设完毕后回填厚±5mm的细石混凝土房地产开发商及施工单位的信誉地面裂缝困扰建筑施工企业的一个难题，成为影响住宅工程质量的通病产生裂缝的部位一般在门口处、墙根处、纵横墙转角处、预埋线管处等位置(a) (b) 3 裂缝产生的特征分析 1）混凝土搅拌工艺的影响 地暖地面施工过程中，在地面一次浇筑成型的情况下，现场搅拌的混凝土地面开裂程度要轻于商品混凝土地面。 2）混凝土坍落度的影响 小坍落度混凝土地面的开裂程度比大坍落度混凝土地面的开裂程度轻，主要表现为大直径泵管浇筑的混凝土（坍落度约为180mm）地面裂纹低于小直径泵管浇筑的混凝土（坍落度约为220mm）地面裂纹。 3）混凝土地面收面过程中，为了施工方便，存在过量洒水收面的现象，表面出现龟裂纹。 4）地面混凝土分两次进行浇筑，第一次浇筑完毕后，经过2-3天的养护后，再浇筑第二次混凝土，地面开裂显著降低。 4 裂缝产生原因分析 1）混凝土的收缩温度变形自生收缩与干缩一样，也是由于水的迁移而引起。但这时水分并非向外蒸发散失，而是因为水泥水化时消耗水分造成凝胶孔的液面下降，产生所谓的自干燥作用，混凝土内的相对湿度降低，体积减小。水灰比变化对两种收缩的影响正相反，即当水灰比降低时干缩减小，而自生收缩增大。如当水灰比大于0.5时,混凝土自干燥作用不明显，其自生收缩与干缩相比小得可以忽略不计；但当水灰比小于0.35时，体内相对湿度会很快降低到80%以下，自生收缩与干缩接近各占一半[2]。在混凝土硬化初期其温度变形和自生变形是产生内应力，造成混凝土开裂的重要驱动力[]。混凝土的温度变形主要由其硬化期间的温度历