蜡镶铸造工艺试验研究.pdf

学兔兔 May2011 VOI．60 NO．5 蜡镶铸造工艺的试验研究 金英福 (延边大学工学院工业设计系，吉林延吉133002) 摘要：蜡镶铸造工艺是目前国内外首饰生产企业进行批量生产所采用的主要工艺方式。在实际生产中，由于不同因素 的影响，蜡镶铸造的产品出现各类质量问题。结合试验及生产经验，探讨了蜡镶铸造易出现的问题及解决措施，分析 了蜡模制作、宝石镶嵌、蜡树种植、石膏型脱蜡焙烧、浇注以及铸件冷却清理各工序特殊工艺要求。为消除铸件的各 种缺陷及完善首饰蜡镶铸造提供重要依据。 关键词：蜡镶；宝石；铸造 中图分类号：TG293 文献标识码：B 文章编号：1001—4977(201 1)05—0508—03 Experimental Study on Wax Setting Technology JIN Ying—fu (Department of Industrial Design，College of Engineering，Yanbian University， Yanji 1 33002，Jilin，China) Abstract：Nowadays，wax setting is the main way used by jewellery manufacture enterprises for mass production at home and abroad．In practical production，different quality problems occur because of the impact of various factors．Combined with experiment and production experiences， some frequently occurred problems in wax setting as well as the solutions were discussed．Special technological requirements were analyzed for the procedures such as wax pattern making，gem setting into wax pattern，planting wax-tree，baking of gypsum mould for dewaxing，pouring，casting cooling and cleaning．It provides important foundations for eliminating all kinds of casting defects and perfecting the wax setting process of jewellry． Key words：wax setting；gem；casting 蜡镶铸造在珠宝首饰铸造领域已逐渐盛行，在镶嵌 过多的滑石粉，橡胶模具每扑过一次滑石粉，可注出 小尺寸、大小均匀、个数较多的宝石时 (群镶)，蜡镶比 3~4个首饰蜡模。 金属镶嵌更具有生产效率，并且具有初学者很容易操作 蜡模制作的第二种方式是利用计算机的快速成形 的特点，因此广泛应用于金和银的首饰铸造。尽管已有 技术，该技术可提高蜡模的精确度。所谓的快速成形 多年经验，许多铸造企业仍有一系列亟待解决的问题。 技术就是利用三维CAD数据，通过快速成形机，由喷 针对蜡镶过程中最常见的问题，通过大量的试验，分析 嘴挤压出半熔