毕业设计（论文）采用聚醚多元醇制备溶剂性PU涂层胶的研究.docVIP

采用聚醚多元醇制备溶剂性PU涂层胶的研究 摘要 PU: 聚氨酯涂层胶（Polyurethane 简称PU） 聚氨酯全称为聚氨基甲酸酯，是分子结构中含有—NHCOO—单元的高分子化合物。本文以聚醚多元醇（牌号GED-30）与聚己二酸乙二醇酯作为聚氨酯的软缎，4 ,4′-二苯基甲烷二异氰酸酯为硬段，采用一步法合成一种聚氨酯涂层胶。同时对其透湿性、防水性、亲水性及其成膜性等进行了研究。实验结果表明：当聚己二酸乙二醇酯与该聚醚多元醇的摩尔比为1：5/4时，使用该聚氨酯涂层的织物的透湿量达到了3500 g/（㎡·d）以上，与水的亲和性较好，但耐静水压只有318Pa。 关键词：聚醚多元醇，聚氨酯，溶剂性，涂层胶 Abstract PU: PU coated plastic (Polyurethane referred to as PU) polyurethane full name polyurethane is a molecular structure containing-NHCOO-unit polymer. In this paper, polyether polyols (Grades GED-30) and polyethylene glycol adipate as a polyurethane satin, 4, 4-diphenyl methane diisocyanate as hard segment, using one-step synthesis of a polyurethane coating Glue. While its breathable, waterproof, and the film-forming hydrophilic, were studied. The results show that: when the polyethylene glycol adipate with the polyether polyol molar ratio of 1:5 / 4, the use of the water vapor permeability of polyurethane coated fabrics amounted to 3500 g / (m ? d ) above hydrostatic pressure 318Pa, but the good affinity with water. Key words: polyether polyols, polyurethane, solvent, plastic coating ? ? 目 录 1. 前 言 1 1.1 聚氨酯(PU)涂料简介 1 1.1.1 聚氨酯涂料的发展 1 1.1.2 聚氨酯行业在我国的发展前景 2 1.1.3 聚氨酯涂层的分类 2 1.1.4聚氨酯涂料优缺点 4 1.1.5 聚氨酯涂料的功能 4 1.2 聚氨酯涂料膜的形成 5 1.2.1 溶剂挥发和热熔的成膜方式 5 1.2.2 化学成膜方式 6 1.3 热固性涂料的稳定性与固化速度问题 6 1.4 聚氨酯涂层涂料面临的挑战 9 1.5 聚氨酯涂料的研究 10 1.6 聚氨酯粉末涂料 11 2. 实验部分 13 2.1实验原理 13 2.2 实验原料 13 2.3 实验设备 14 2.4 实验内容及方法 14 2.4.1 制品的合成 14 2.4.2 制品性能检测 16 3. 结果与讨论 18 3.1 透湿性与聚氨酯中聚醚含量的关系 18 3.2 聚醚型聚氨酯的亲水机理 18 3.3 聚醚含量对织物涂层防水性的影响 18 3.4 涂层耐水性与聚醚含量关系 19 3.5 涂层耐溶剂性讨论 19 3.6 耐寒性讨论 20 4. 结论 21 参考文献 22 感谢 24  1. 前 言 聚氨酯是一种新兴的有机高分子材料，被誉为“第五大塑料”，因其卓越的性能而被广泛应用于国民经济众多领域。根据所用原料的不同，可有不同性质的产品，一般为聚酯型和聚醚型两类。可用于制造塑料、橡胶、纤维、硬质和软质泡沫塑料、胶粘剂和涂料等R1-N=C=O + R2-OH —— → R1-N—C-O-R2 I II H O 本实验首先使聚己二酸乙二醇酯与过量的MDI反应生成两端为MDI的链，此时端基为-NCO。再引入聚醚与分子链上的端基反应下去，得到形如下图的大分子聚合物： ～G-M～G-M-D～M-D-M～D-M-G～M-G～ 其中D代表聚酯；G代表聚醚；M代表MDI。制品通过实验制备以后，使用交联剂将线形大分子链交联成空间网状