新型Zn-22Al-Mg-Re合金涂层性能研究.PDF

新型Zn-22Al-Mg-Re 合金涂层性能研究 胡新芳，李辛庚，樊志彬，王晓明，王学刚 （国网山东省电力公司电力科学研究院 山东 济南 250002） 摘要：使用高速电弧喷涂技术在Q420 钢基体上制备了新型Zn-22Al-Mg-Re 合金涂层，通过SEM，Cu 加速乙酸盐雾实验和电化学工 作站等手段研究了其微观组织形貌、结合强度、耐蚀性能，并与纯Zn 和Zn-15Al 涂层进行了比较。结果表明，Zn-22Al-Mg-Re 合金 涂层的结合强度高，腐蚀电位低，腐蚀电流小；腐蚀产物较为稳定，呈细小致密的针状，具有良好的自封闭性；合金涂层的阴极保护 能力和耐蚀性能均优于纯Zn 和Zn-15Al 涂层。 关键词：Zn-22Al-Mg-Re 合金涂层；结合强度；自封闭；耐蚀性能 中图分类号：TG172.3 文献标识码：A Performance Study of Novel Zn-22Al-Mg-Re Alloy Coating Hu Xinfang, Li Xingeng, Fan Zhibin,Wang Xiaoming,Wang Xuegang (Shandong Electric Power Research Institute, Shandong Jinan 250002, China) Abstract: The novel Zn-22Al-Mg-Re alloy coating were prepared on the Q420 substrate by arc spraying technology, and the coating Microstructure, Bonding strength and corrosion resistance were studied by SEM, copper accelerated acetic acid salt spray test(CASS) and electrochemical workstation etc, compared with Zn and Zn-15Al coating. The test results show that, the Zn-22Al-Mg-Re corrosion potential and corrosion current is minimum, because of its ability to form a very stable, 1 v adherent , small acicular, well self-sealing protecting layer on the steel substrate, the cathodic protection ability and 9 corrosion resistance of Zn-22Al-Mg-Re coating is better than Zn , Zn-15Al coating. 3 Key words: Zn-22Al-Mg-Re; Bonding strength; self-sealing; corrosion resistance 4 由于重工业快速发展和全球自然环境的恶化等原 研究涂层微观形貌、结合强度和耐蚀性能。 0 因，输变电钢构件运行环境条件严重恶化，构件防护涂 1 实验方法 0. 层的腐蚀速率有明显加速趋势，除发生极端恶劣的灾害 1.1试样制备 1 天气之外，由于环境腐蚀造成输电杆塔的强度缺失是导 实验材料采用直径为 3 mm 的纯 Zn ，Zn-15Al 和 1 致事故的直接原因。传统镀锌技术已不能满足其防护寿 Zn-22Al-Mg-Re 合金丝材。基体选用目前输变电钢构件 6 命的全周期设计要求，所使用的镀锌杆塔大部分实际使 常用的 Q420 钢。采用喷砂对试样表面进行处理，使用 1 0 用寿命远远低于其设计寿