激光微孔脱细胞真皮基质生物力学测试.docVIP

激光微孔脱细胞真皮基质生物力学测试[摘要]目的:研究激光微孔脱细胞基质的生物力学性质变化,制作合适规格的脱细胞基质。方法:对不同间距的脱细胞真皮基质进行应力-应变和应力-松弛实验等检测,确定最佳孔径的脱细胞真皮基质。结果:确定350μm间距的脱细胞真皮基质有良好的生物力学性能。结论:超脉冲CO2激光可以对脱细胞真皮基质进行精细的微加工,脱细胞真皮基质适用于构建组织工程支架。 [关键词]脱细胞真皮基质;激光;微孔;生物力学 [中图分类号]Q813.1[文献标识码]A [文章编号]1008-6455(2010)05-0694-03 The biomechanical test on the laser microcavity acellular dermal matrix LIN Huang,LI Wen-zhi,YAN Xiu-juan (Department of Plastic and Cosmetic ,Anzhen Hospital,Capital University of Medical Science,Beijing 100029,China) Abstract:ObjectiveTo study the variations of the biomechanism of the laser microcavity of acellular dermal matrix and to fabricate a proper standard acellular dermal matrix.MethodsTo make an experiment on the various distance of the acellular dermal matrix with the tension-change and tension-relaxon,and to determine the best distance of the acellular dermal matrix.ResultsThe acellular dermal matrix of distance between 350μm is ofexcellent biomechanicalproperities.ConclusionsThe super pulse CO2 laser can work on the acellular dermal matrix precisely,the microcavity acellular dermal matrix is applicable to the reconstruction of the tissue engineered frameworks. Key words: ADM;laser;microcavity; biomechanical 脱细胞真皮基质(acellular dermal matrix,ADM)是去除了真皮中具有抗原性的细胞成分,而保留了原有胶原纤维、弹力纤维等结构的真皮支架。但脱细胞真皮基质结构较致密,再植回体内后血管化受影响,笔者用超脉冲CO2激光改造脱细胞真皮基质结构,重塑微血管通道,促进脱细胞基质的血管化。但是微孔存在是否影响脱细胞真皮基质的生物力学特性,对此笔者作出进一步研究。 1材料和方法 1.1 脱细胞真皮基质的制备:新西兰大白兔背部皮肤去毛、去脂后, 制成薄中厚皮片,PBS 液冲洗后置于0.125%胰蛋白酶溶液中,4℃低温下24～48h, 脱去表皮和真皮内所有细胞成分。皮片室温下孵育于0.15% Triton X-100 溶液中, 持续震摇24h即可制得ADM, PBS 液充分漂洗后备用。 1.2 激光微孔脱细胞真皮基质的制备和分组:脱细胞真皮基质30片,分为5组:4组为实验组,CO2激光打孔(波长10.6μm,功率700W,光斑直径200μm,脉宽60ms),每孔间距分别为200μm、350μm、500μm和650μm;1组为对照组,不做任何处理。 1.3 主要实验设备:INSTRON 4302 拉伸机,夹持标本用的特制夹头,适用100N的传感器,载荷范围设定为20N(图1)。 1.4 测试步骤:①对于每个标本分别测量3 次厚度和宽度, 计算其平均值;②强度实验: 以10 mm/min 速度将脱细胞真皮基质拉断,记录此时力大小;③应力实验: 将脱细胞真皮基质拉到2.0MPa柯希应力时卸载, 预调3 次, 记录第4次实验数值;④松弛实验: 给标本一个速度脉冲, 大小为300 mm/min, 松弛时间设为3min。 1.5 数据处理:①应力-应变曲线: 对在生理范围内的应力( 300 kPa)