常化处理对10Cr17铁素体不锈钢织构及深冲性能的影响.pdfVIP

常化处理对10Cr17铁素体不锈钢织构及深冲性能的 影响 李双武 冯运莉 河北联合大学冶金与能源学院，河北省现代冶金技术重点实验室，河北，唐山063009 摘要 研究了热轧10Cr17铁素体不锈钢钢带在不经退火直接酸洗冷轧和经罩式炉退火后再酸洗冷轧、最后经再结晶退火后 制品的深冲性能，以及各个工序中钢带的金相组织、力学性能和织构，结果表明，利用罩式炉退火工艺生产的最终冷轧退火 钢带中轧制面的{111}面织构充分发达、{001}面织构被削弱，材料的抗起皱性能较好、r值较高，深冲时表面不易产生平行于 轧制方向的狭窄条纹起皱缺陷，表现出较好的深冲性能。 关键词 10Cr17铁素体不锈钢；常化处理；织构；深冲性能 Effectofnormalizingontexureanddeep-drawingpropertyona10Cr17 ferriticstainlesssteel LIShuang-wu FENGYun-li CollegeofMetallurgyandEnergy,HebeiUnitedUniversity,HebeiUnitedUniversity,HebeikeyLaboratoryofModemMetallurgyTechnology,Hebei,Tangshan 063009,China ABSTRACT Themicrostructure,mechanicalpropertiesandtextureof10Cr17ferriticstainlessstripswereresearchedundertwo processescondition,withoutnormalizingandwithnormalizinginthecover-typeannealingfurnancebeforepickingandrolling.The resultsshowedthatthetexture{111}wasstrengthedandthetexture{001}wasweakenedofcoverannealsstrip,andhighvalueofr wasobtained.Meanwhile,thecrimpingdefectparallelingtorollingdirectionwasuneasyappearedduringstretchingandthestripshow gooddeep-drawingperformanceaftercovernormalizing. KEYWORDS 10Cr17ferriticstainlesssteel;normalizing;texture;deep-drawingingproperty 第十六届冶金反应工程学会议论文集 不锈钢表面产生皱折的原因，其目的在于提高铁素体不锈钢的成形性能及表面质量。 1实验材料和方案 实验材料为唐山不锈钢有限责任公司生产的10Crl7铁素体不锈钢热轧板卷，其化学成分见表1。在线 切割机上切取80mm×150mm的长方形试样。 表l 10crl7的化学成分(坝％) TablelChemical of10Crl7(、Vt％) composition C Si Mn P S Ni cr 0．12 i 1．00 1．OO 0．040 0．030 0．75 17．00 将试样分为两组，设计两种工艺实验方案。一组试样经酸洗、80％压下率冷轧，然后在箱式炉中进行 压下率冷轧，最后在箱式炉中进行800℃×1h的退火即工艺2。 的四辊冷轧机上进行。试样经金相研磨、抛光，再用王水腐蚀后，在Axiovert200l讥AT型光学显微镜下观察 仪上进行，力学性能及塑性应变比r值的测量是在HY20080型拉伸实验机上进行的。 2试验结果与分析 2．1显微组织 10Crl7铁素体不锈钢不同状态下的显微组织如图l所示。 图l lOCrl7铁