620℃级超超临界汽轮机用ZG13Cr9Mo2Co1NiVNbNB钢阀壳的试制和生产.pdfVIP

铸造工程 材料与工艺 Foundry Engineering 620 ℃级超超临界汽轮机用ZG13Cr9Mo2Co1NiVNbNB 钢阀壳的试制和生产 徐德民 （上海宏钢电站设备铸锻有限公司，上海 200240） 摘要：为满足620 ℃等级超超临界汽轮机机阀壳的性能要求，开发了ZG13Cr9Mo2Co1NiVNbNB 钢。通过工艺试验，阀壳铸件已进行了试制和生产，检测结果表明，所生产的铸件化学成分、 力学性能及显微组织均满足技术要求。 关键词：汽轮机；ZG13Cr9Mo2Co1NiVNbNB钢；阀壳；试制 中图分类号：TG142.73 文献标识码：B 文章编号：1673-3320（2017）03-0018-04 Trial-manufacture and Production of Valve Housing of ZG13Cr9Mo2Co1NiVNbNB Steel Used for 620℃ Grade Super Ultra-critical Steam Turbine XU Demin (Shanghai Honggang Power Station Equipment Castings Forgings Co., Ltd., Shanghai, 200240 China) Abstract: A type of ZG13Cr9Mo2Co1NiVNbNB steel has been developed to meet performance requirements of valve housing used for 620 ℃ grade super ultra-critical steam turbine. After the technological test the trial-manufacture and production of cast valve housings have been performed. It was showed from the detection and measurements that chemical composition, mechanical properties and microstructure of the produced valve housings all reached the technical requirements. Keywords: steam turbine; ZG13Cr9Mo2Co1NiVNbNB steel; valve housing; trial-manufacture 大功率、高参数、高可靠性、高热效率和清 钼、钴固溶强化，形成了多种碳化物强化相。钢 洁环保已经成为当今汽轮机技术的发展方向，大 中加入氮可增加 （V ，N b ）N 沉淀强化效果；加 力发展低煤耗、低污染的超超临界火电机组技术 硼强化晶界；钴除了固溶强化外，还提高基体的 是我国实现节能减排战略目标和保障国家能源安 再结晶温度，延缓马氏体回火时α相的回复，提 全的重要措施之一，开发高效低排放汽轮机机组 高钢的蠕变抗力；加镍可消除δ铁素体，与铬、 所需材料成为当务之急。620 ℃等级超超临界汽轮 钼一起使钢在正火回火热处理后获得强度和韧性 机是上海电气电站设备有限公司汽轮机厂全新设 配合良好的回火马氏体组织。CB2钢化学成分见 计的汽轮机机组，阀壳是该机组的关键铸件，材